MOVPE-grown Si-doped \b{eta}-(Al0.26Ga0.74)2O3 thin films and heterostructures

Abstract

We report on n-type degenerate doping in MOVPE grown \b{eta}-(Al0.26Ga0.74)2O3 epitaxial thin films and modulation doping in \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructure. Alloy composition is confirmed using HRXRD measurements. Carrier concentration in the thin films is proportional to the silane molar flow. Room temperature hall measurements showed a high carrier concentration of 6x1018-7.3x1019 cm-3 with a corresponding electron mobility of 53-27 cm2/V.s in uniformly-doped \b{eta}-(Al0.26Ga0.74)2O3 layers. Modulation doping is used to realize a total electron sheet charge of 2.3x1012 cm-2 in a \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructure using a uniformly-doped \b{eta}-(Al0.26Ga0.74)2O3 barrier layer and a thin spacer layer.

References in corpus (2)

• Intrinsic Electron Mobility Limits in beta-Ga2O3
• Modulation-doped beta-(Al0.2Ga0.8)2O3/Ga2O3 Field-Effect Transistor

Cited by in corpus (10)

• Multi-kV class $\beta$-Ga${}_2$O${}_3$ MESFETs with a Lateral Figure of Merit up to 355 MW/cm${}^2$
• Low Temperature Homoepitaxy Of (010) $\beta$-Ga${}_2$O${}_3$ By Metalorganic Vapor Phase Epitaxy : Expanding The Growth Window
• Highly tunable polarization-engineered two-dimensional electron gas in $\epsilon$-AlGaO3 / $\epsilon$-Ga2O3 heterostructures
• 4.4 kV $\beta$-Ga${}_2$O${}_3$ Power MESFETs with Lateral Figure of Merit exceeding 100 MW/cm${}^2$
• Growth and Characterization of Metalorganic Vapor-Phase Epitaxy-Grown \b{eta}-(AlxGa1-x)2O3/\b{eta}-Ga2O3 Heterostructure Channels
• Delta-doped \b{eta}-Ga2O3 thin films and \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructures grown by metalorganic vapor-phase epitaxy
• Alloyed B-(AlxGa1-x)2O3 bulk Czochralski single B-(Al0.1Ga0.9)2O3 and polycrystals B-(Al0.33Ga0.66)2O3, B-(Al0.5Ga0.5)2O3), and property trends
• Delta-doped \b{eta}-Ga2O3 Films With Low FWHM Charge Profile Grown By Metalorganic Vapor-Phase Epitaxy
• Impurity Band Conduction in Si-doped \b{eta}-Ga2O3 Films
• Theoretical Investigation of Optical Intersubband Transitions and Infrared Photodetection in $\beta$-(AlxGa1-x)2O3/Ga2O3 Quantum Well Structures