Microwave characterization of tantalum superconducting resonators on silicon substrate with niobium buffer layer

Abstract

Tantalum thin films sputtered on unheated silicon substrates are characterized with microwaves at around 10 GHz in a 10 mK environment. We show that the phase of tantalum with a body-centered cubic lattice ($\alpha$-Ta) can be grown selectively by depositing a niobium buffer layer prior to a tantalum film. The physical properties of the films, such as superconducting transition temperature and crystallinity, change markedly with the addition of the buffer layer. Coplanar waveguide resonators based on the composite film exhibit significantly enhanced internal quality factors compared with a film without the buffer layer. The internal quality factor approaches $2\times 10^7$ at a large-photon-number limit. While the quality factor decreases at the single-photon level owing to two-level system (TLS) loss, we have identified the primary cause of TLS loss to be the amorphous silicon layer at the film-substrate interface, which originates from the substrate cleaning before the film deposition rather than the film itself. The temperature dependence of the internal quality factors shows a marked rise below 200 mK, suggesting the presence of TLS-TLS interactions. The present low-loss tantalum films can be deposited without substrate heating and thus have various potential applications in superconducting quantum electronics.

arXiv comment7 pages, 4 figures + Supplementary Material (8 pages, 5 figures)

References in corpus (27)

• Charge insensitive qubit design derived from the Cooper pair box
• Decoherence in Josephson Qubits from Dielectric Loss
• Coherent Josephson qubit suitable for scalable quantum integrated circuits
• New material platform for superconducting transmon qubits with coherence times exceeding 0.3 milliseconds
• Towards understanding two-level-systems in amorphous solids -- Insights from quantum circuits
• Transmon qubit with relaxation time exceeding 0.5 milliseconds
• Experimental evidence for a surface distribution of two-level systems in superconducting lithographed microwave resonators
• An analysis method for asymmetric resonator transmission applied to superconducting devices
• Microwave Dielectric Loss at Single Photon Energies and milliKelvin Temperatures
• Improved superconducting qubit coherence using titanium nitride
• Materials loss measurements using superconducting microwave resonators
• Reducing intrinsic loss in superconducting resonators by surface treatment and deep etching of silicon substrates
• Evidence for interacting two-level systems from the 1/f noise of a superconducting resonator
• Improving the Coherence Time of Superconducting Coplanar Resonators
• Determining interface dielectric losses in superconducting coplanar waveguide resonators
• Fabrication and Characterization of Aluminum Airbridges for Superconducting Microwave Circuits
• Characterization and Reduction of Capacitive Loss Induced by Sub-Micron Josephson Junction Fabrication in Superconducting Qubits
• Solid-state qubits integrated with superconducting through-silicon vias
• Investigation of microwave loss induced by oxide regrowth in high-Q Nb resonators
• Disentangling Losses in Tantalum Superconducting Circuits
• Low-loss superconducting resonant circuits using vacuum-gap-based microwave components
• Qubit-compatible substrates with superconducting through-silicon vias
• Accessible Color Sequences for Data Visualization
• Analytical determination of participation in superconducting coplanar architectures
• Two-Level Systems in Nucleated and Non-Nucleated Epitaxial alpha-Tantalum films
• Modelling Enclosures for Large-Scale Superconducting Quantum Circuits
• Investigation of the deposition of $\alpha$-tantalum (110) films on a-plane sapphire substrate by molecular beam epitaxy for superconducting circuit

Cited by in corpus (4)

• Low-Loss Superconducting Resonators Fabricated from Tantalum Films Grown at Room Temperature
• Investigation of tantalum films growth for coplanar resonators with internal quality factors above ten million
• In situ Al${}_2$O${}_3$ passivation of epitaxial tantalum and aluminum films enables long-term stability in superconducting microwave resonators
• Enhanced Tantalum Superconducting Resonator Performance via All-Surface Organic Monolayer Passivation