In situ Al${}_2$O${}_3$ passivation of epitaxial tantalum and aluminum films enables long-term stability in superconducting microwave resonators

Abstract

Long-term stability of superconducting microwave resonators is essential for scalable quantum technologies; however, surface and interface degradation continue to limit device stability. Here, we demonstrate exceptional stability in microstrip resonators fabricated from epitaxial tantalum and aluminum films, protected by in situ deposited Al${}_2$O${}_3$ under ultra-high vacuum. These resonators initially exhibit internal quality factors (Qi) exceeding one million and maintain high performance with minimal degradation after up to fourteen months of air exposure. In contrast, devices relying on native surface oxides show substantial declines in Qi over time, indicating increased microwave losses. X-ray photoelectron spectroscopy reveals that the in situ Al${}_2$O${}_3$ effectively suppresses interfacial oxidation and preserves the chemical integrity of the underlying superconducting films, whereas native oxides permit progressive oxidation, leading to device degradation. These findings establish a robust, scalable passivation strategy that addresses a longstanding materials challenge in the development of superconducting quantum circuits.

arXiv comment21 pages, 5 figures

References in corpus (19)

• Decoherence in Josephson Qubits from Dielectric Loss
• New material platform for superconducting transmon qubits with coherence times exceeding 0.3 milliseconds
• Planar Superconducting Resonators with Internal Quality Factors above One Million
• Experimental evidence for a surface distribution of two-level systems in superconducting lithographed microwave resonators
• Efficient and robust analysis of complex scattering data under noise in microwave resonators
• Systematic Improvements in Transmon Qubit Coherence Enabled by Niobium Surface Encapsulation
• Suppression of 1/f noise in solid state quantum devices by surface spin desorption
• Disentangling Losses in Tantalum Superconducting Circuits
• Substrate surface engineering for high-quality silicon/aluminum superconducting resonators
• Quantum electrodynamics of a superconductor-insulator phase transition
• Chemical profiles of the oxides on tantalum in state of the art superconducting circuits
• A fluxonium-based artificial molecule with a tunable magnetic moment
• Mitigation of interfacial dielectric loss in aluminum-on-silicon superconducting qubits
• Dielectric loss extraction for superconducting microwave resonators
• Characterization of low loss microstrip resonators as a building block for circuit QED in a 3D waveguide
• Manufacturing high-Q superconducting α-tantalum resonators on silicon wafers
• Microwave characterization of tantalum superconducting resonators on silicon substrate with niobium buffer layer
• Low loss hybrid Nb/Au superconducting resonators for quantum circuit applications
• Stable and low loss oxide layer on α-Ta (110) film for superconducting qubits