Quantum well confinement and competitive radiative pathways in the luminescence of black phosphorus layers

Abstract

Black phosphorus (BP) stands out from other 2D materials by the wide amplitude of the band-gap energy (Delta(Eg)) that sweeps an optical window from Visible (VIS) to Infrared (IR) wavelengths, depending on the layer thickness. This singularity made the optical and excitonic properties of BP difficult to map. Specifically, the literature lacks in presenting experimental and theoretical data on the optical properties of BP on an extended thickness range. Here we report the study of an ensemble of photoluminescence spectra from 79 passivated BP flakes recorded at 4 K with thicknesses ranging from 4 nm to 700 nm, obtained by mechanical exfoliation. We observe that the exfoliation steps induce additional defects states that compete the radiative recombination from bound excitons observed in the crystal. We also show that the evolution of the photoluminescence energy versus thickness follows a quantum well confinement model appreciable from a thickness predicted and probed at 25 nm. The BP slabs placed in different 2D heterostructures show that the emission energy is not significantly modulated by the dielectric environment. Introduction Confinement effects

11 pages, 3 figures - Main text 12 pages, 5 figures - Supporting information

References in corpus (8)

• Effective Passivation of Exfoliated Black Phosphorus Transistors against Ambient Degradation
• Environmental instability of few-layer black phosphorus
• Tunable optical properties of multilayers black phosphorus thin films
• Infrared fingerprints of few-layer black phosphorus
• Field Effect Optoelectronic Modulation of Quantum-Confined Carriers in Black Phosphorus
• Electronic structures of air-exposed few-layer black phosphorus by optical spectroscopy
• Excitons in bulk black phosphorus evidenced by photoluminescence at low temperature
• Light emission properties of mechanical exfoliation induced extended defects in hexagonal boron nitride flakes

Cited by in corpus (2)

• Anisotropic effects in two-dimensional materials
• Straightforward Method to Orient Black Phosphorus from Bulk to Thin Layers using a Standard Green Laser