Evolution of Ge wetting layers growing on smooth and rough Si (001) surfaces: isolated {105} facets as a kinetic factor of stress relaxation

Abstract

The results of STM and RHEED studies of a thin Ge film grown on the Si/Si(001) epitaxial layers with different surface relief are presented. Process of the partial stress relaxation was accompanied by changes in the surface structure of the Ge wetting layer. Besides the well-known sequence of surface reconstructions ($2\times 1\to 2\times N\to M\times N$ patches) and hut clusters faceted with {105} planes, the formation of isolated {105} planes, which faceted the edges of $M\times N$ patches, has been observed owing to the deposition of Ge on a rough Si/Si (001) surface. A model of the isolated {105} facet formation has been proposed based on the assumption that the mutual arrangement of the monoatomic steps on the initial Si surface promotes the wetting layer formation with the inhomogeneously distributed thickness that results in the appearance of $M\times N$ patches partially surrounded by deeper trenches than those observed in the usual Ge wetting layer grown on the smooth Si(001) surface. Isolated {105} facets are an inherent part of the Ge wetting layer structure and their formation decreases the surface energy of the Ge wetting layer.

arXiv comment27 pages, 8 figures

References in corpus (11)

• Strain induced stabilization of stepped Si and Ge surfaces near (001)
• Nucleation of Ge quantum dots on the Si(001) surface
• CMOS compatible dense arrays of Ge quantum dots on the Si(001) surface: Hut cluster nucleation, atomic structure, and array life cycle during UHV MBE growth
• Nucleation of Ge clusters at high temperatures on Ge/Si(001) wetting layer
• Tight binding studies of strained Ge/Si(001) growth
• An initial phase of Ge hut array formation at low temperature on Si(001)
• Evidence for Kinetic Limitations as a Controlling Factor of Ge Pyramid Formation: a Study of Structural Features of Ge/Si(001) Wetting Layer Formed by Ge Deposition at Room Temperature Followed by Annealing at 600 °C
• On atomic structure of Ge huts growing on the Ge/Si(001) wetting layer
• 3D Nanostructures on Ge/Si(100) Wetting Layers: Hillocks and Pre-Quantum Dots
• Entropy controlled fully reversible nanostructure formation of Ge on miscut vicinal Si (001) surfaces
• The formation of intermediate layers in covered Ge/Si heterostructures with low-temperature quantum dots: a study using high-resolution transmission electron microscopy and Raman spectroscopy

Cited by in corpus (1)

• Atomistic study of dislocation formation during Ge epitaxy on Si