Exploration of co-sputtered Ta${}_2$O${}_5$-ZrO${}_2$ thin films for gravitational-wave detectors

Abstract

We report on the development and extensive characterization of co-sputtered tantala-zirconia thin films, with the goal to decrease coating Brownian noise in present and future gravitational-wave detectors. We tested a variety of sputtering processes of different energies and deposition rates, and we considered the effect of different values of cation ratio $\eta =$ Zr/(Zr+Ta) and of post-deposition heat treatment temperature $T_a$ on the optical and mechanical properties of the films. Co-sputtered zirconia proved to be an efficient way to frustrate crystallization in tantala thin films, allowing for a substantial increase of the maximum annealing temperature and hence for a decrease of coating mechanical loss. The lowest average coating loss was observed for an ion-beam sputtered sample with $\eta =0.485\pm 0.004$ annealed at 800 ${}^{\circ }$C, yielding $\overline{\phi }=1.8\times 10^{-4}$. All coating samples showed cracks after annealing. Although in principle our measurements are sensitive to such defects, we found no evidence that our results were affected. The issue could be solved, at least for ion-beam sputtered coatings, by decreasing heating and cooling rates down to 7 ${}^{\circ }$C/h. While we observed as little optical absorption as in the coatings of current gravitational-wave interferometers (0.5 parts per million), further development will be needed to decrease light scattering and avoid the formation of defects upon annealing.

References in corpus (36)

• Observation of Gravitational Waves from a Binary Black Hole Merger
• GW170817: Observation of Gravitational Waves from a Binary Neutron Star Inspiral
• Advanced Virgo: a 2nd generation interferometric gravitational wave detector
• Multi-messenger Observations of a Binary Neutron Star Merger
• GWTC-1: A Gravitational-Wave Transient Catalog of Compact Binary Mergers Observed by LIGO and Virgo during the First and Second Observing Runs
• Advanced LIGO
• GW170817: Measurements of Neutron Star Radii and Equation of State
• GWTC-2: Compact Binary Coalescences Observed by LIGO and Virgo During the First Half of the Third Observing Run
• Binary Black Hole Mergers in the first Advanced LIGO Observing Run
• Sensitivity and Performance of the Advanced LIGO Detectors in the Third Observing Run
• Thermal noise in interferometric gravitational wave detectors due to dielectric optical coatings
• Titania-doped tantala/silica coatings for gravitational-wave detection
• Quantum Measurement Theory in Gravitational-Wave Detectors
• Structural and dielectric properties of amorphous ZrO2 and HfO2
• Prospects for doubling the range of Advanced LIGO
• Mechanical Loss in Tantala/Silica Dielectric Mirror Coatings
• Thermo-optic noise in coated mirrors for high-precision optical measurements
• Amorphous optical coatings of present gravitational-wave interferometers
• Frequency and surface dependence of the mechanical loss in fused silica
• Cosmic Explorer: The U.S. Contribution to Gravitational-Wave Astronomy beyond LIGO
• Mechanical loss in state-of-the-art amorphous optical coatings
• Mechanical Dissipation in Silicon Flexures
• Effect of heat treatment on mechanical dissipation in Ta${}_2$O${}_5$ coatings
• Brownian Thermal Noise in Multilayer Coated Mirrors
• Measurement of Thermal Noise in Multilayer Coatings with Optimized Layer Thickness
• Thermal noise in half infinite mirrors with non-uniform loss: a slab of excess loss in a half infinite mirror
• Progress in the measurement and reduction of thermal noise in optical coatings for gravitational-wave detectors
• Observation of a Correlation Between Internal friction and Urbach Energy in Amorphous Oxides Thin Films
• Direct Measurement of Coating Thermal Noise in Optical Resonators
• High-Reflection Coatings for Gravitational-Wave Detectors: State of The Art and Future Developments
• Measurements of mechanical thermal noise and energy dissipation in optical dielectric coatings
• Evidence for structural transition in crystalline tantalum pentoxide films grown by RF magnetron sputtering
• Enhanced Medium Range Order in Vapor Deposited Germania Glasses at Elevated Temperatures
• Correlated evolution of structure and mechanical loss of a sputtered silica film
• Structural evolution of binary oxide nanolaminates with annealing and its impact on room-temperature internal friction
• A method for the experimental measurement of bulk and shear loss angles in amorphous thin films

Cited by in corpus (4)

• Low mechanical loss TiO${}_2$:GeO${}_2$ coatings for reduced thermal noise in Gravitational Wave Interferometers
• Comprehensive study of amorphous metal oxide and Ta${}_2$O${}_5$-based mixed oxide coatings for gravitational-wave detectors
• Effects of mixing and annealing on the optical and mechanical properties of TiO${}_2$:Ta${}_2$O${}_5$ amorphous coatings
• Imaging Scatterometer for Observing In-Situ Changes to Optical Coatings During Air Annealing