$WS{e}_2$ Monolayers Grown by Molecular Beam Epitaxy on hBN

Abstract

A three-step process was developed for growing high-quality, optically uniform WSe2 monolayers by molecular beam epitaxy (MBE) with advantage of using hexagonal boron nitride (hBN). The process was optimized to maximize the efficiency of photoluminescence and promote formation of hexagonal WSe2 domains. Atomic force microscopy (AFM) was employed to estimate the dispersion of WSe2 hexagonal domains orientation. Monolayer character of the film was identified using optical methods and verified with high-resolution transmission electron microscopy (TEM) cross-section. Temperature-and-magnetic-field-dependent studies revealed the behaviour of exciton complexes to be analogical to that of exfoliated counterparts. Direct growth on hBN combined with uniform optical response proves this WSe2 superior to mechanically exfoliated WSe2 in terms of convenience of use and reproducibility. Provided results establish a significant progress in optical quality of epitaxially grown transition metal dichalcogenides (TMDs) monolayers and fabrication of large-scale functional devices.

Article and SI, 18 pages in total, 10 figures in total

References in corpus (6)

• Atomically thin p-n junctions with van der Waals heterointerfaces
• Single-crystal hexagonal boron nitride monolayer epitaxially grown on Cu (111) thin film across a wafer
• Layer-by-layer epitaxial growth of scalable WSe2 on sapphire by molecular-beam epitaxy
• Tailoring the dielectric screening in WS${}_2$-graphene heterostructures
• Magneto-spectroscopy of exciton Rydberg states in a CVD grown WSe2 monolayer
• Photoluminescence efficiency of MBE-grown MoSe${}_2$ monolayers featuring sharp excitonic lines and diverse grain structures