Anti-reflection coating with mullite and Duroid for large-diameter cryogenic sapphire and alumina optics

Abstract

We developed a broadband two-layer anti-reflection (AR) coating for use on a sapphire half-wave plate (HWP) and an alumina infrared (IR) filter for the cosmic microwave background (CMB) polarimetry. Measuring the faint CMB B-mode signals requires maximizing the number of photons reaching the detectors and minimizing spurious polarization due to reflection with an off-axis incident angle. Sapphire and alumina have high refractive indices of 3.1 and are highly reflective without an AR coating. This paper presents the design, fabrication, quality control, and measured performance of an AR coating using thermally-sprayed mullite and Duroid 5880LZ. This technology enables large optical elements with diameters of 600 mm. We also present a newly developed thermography-based nondestructive quality control technique, which is key to assuring good adhesion and preventing delamination when thermal cycling. We demonstrate the average reflectance of about 2.6% (0.9%) for two observing bands centered at 90/150 (220/280) GHz. At room temperature, the average transmittance of a 105 mm square test sample at 220/280 GHz is 83%, and it will increase to 90% at 100 K, attributed to reduced absorption losses. Therefore, our developed layering technique has proved effective for 220/280 GHz applications, particularly in addressing dielectric loss concerns. This AR coating technology has been deployed in the cryogenic HWP and IR filters of the Simons Array and the Simons observatory experiments and applies to future experiments such as CMB-S4.

References in corpus (22)

• The Simons Observatory: Science goals and forecasts
• BICEP / Keck XIII: Improved Constraints on Primordial Gravitational Waves using Planck, WMAP, and BICEP/Keck Observations through the 2018 Observing Season
• A Probe of Primordial Gravity Waves and Vorticity
• CMB-S4 Science Case, Reference Design, and Project Plan
• Improved limits on the tensor-to-scalar ratio using BICEP and Planck
• The POLARBEAR-2 and the Simons Array Experiment
• Modulation of CMB polarization with a warm rapidly-rotating half-wave plate on the Atacama B-Mode Search (ABS) instrument
• Direct Signature of Evolving Gravitational Potential from Cosmic Microwave Background
• Performance of a continuously rotating half-wave plate on the POLARBEAR telescope
• Systematic effects from an ambient-temperature, continuously-rotating half-wave plate
• The Simons Observatory Large Aperture Telescope Receiver
• Design and development of an ambient-temperature continuously-rotating achromatic half-wave plate for CMB polarization modulation on the POLARBEAR-2 experiment
• The Simons Observatory: gain, bandpass and polarization-angle calibration requirements for B-mode searches
• Epoxy-based broadband anti-reflection coating for millimeter-wave optics
• Cryogenic infrared filter made of alumina for use at millimeter wavelength
• Small Aperture Telescopes for the Simons Observatory
• A cryogenic continuously rotating half-wave plate for the POLARBEAR-2b cosmic microwave background receiver
• Two-layer anti-reflection coating with mullite and polyimide foam for large-diameter cryogenic infrared filters
• Design and Fabrication of Metamaterial Anti-Reflection Coatings for the Simons Observatory
• Broadband anti-reflective coatings for cosmic microwave background experiments
• Composite Reflective/Absorptive IR-Blocking Filters Embedded in Metamaterial Antireflection Coated Silicon
• Broadband multi-layer anti-reflection coatings with mullite and duroid for half-wave plates and alumina filters for CMB polarimetry

Cited by in corpus (1)

• The Simons Observatory: Development and Optical Evaluation of Achromatic Half-Wave Plates