Oxygen vacancy driven mobility enhancement in epitaxial La-doped BaSnO3 from vacuum annealing

Abstract

Wide bandgap (~3.1 eV) La-doped BaSnO3 (LBSO) has attracted increasing attention as one of the transparent oxide semiconductors since its bulk single crystal shows a high carrier mobility (~320 cm2 V-1 s-1) with a high carrier concentration (~10^20 cm-3). For this reason, many researchers have fabricated LBSO epitaxial films thus far, but the obtainable carrier mobility is substantially low compared to that of single crystals due to the formation of the lattice/structural defects. Here we report that the mobility suppression in LBSO films can be lifted by a simple vacuum annealing process. The vacuum annealing of the LBSO films on MgO substrate increased the carrier concentrations due to the oxygen vacancy formation, which leads to simultaneous lateral grain growth. As a result, the carrier mobility was greatly improved by the vacuum annealing, which does not occur after heat treatment in air. These results expand our current knowledge on the point defect formation in epitaxial LBSO films and show that vacuum annealing is a powerful tool for enhancing the mobility values of LBSO films.

References in corpus (5)

• High Mobility in a Stable Transparent Perovskite Oxide
• Physical properties of transparent perovskite oxides (Ba,La)SnO3 with high electrical mobility at room temperature
• Transparent perovskite barium stannate with high electron mobility and thermal stability
• Large thickness dependence of the carrier mobility in a transparent oxide semiconductor, La-doped BaSnO3
• Thermopower modulation clarification of the intrinsic effective mass in a transparent oxide semiconductor, BaSnO3

Cited by in corpus (6)

• One-step epitaxy of high-mobility La-doped BaSnO3 films by high-pressure magnetron sputtering
• Buffer layer-less fabrication of high-mobility transparent oxide semiconductor, La-doped BaSnO3
• Epitaxial Films and Devices of Transparent Conducting Oxides: La:BaSnO${}_3$
• Employing High-temperature-grown SrZrO${}_3$ Buffer to Enhance the Electron Mobility in La:BaSnO${}_3$-based Heterostructures
• $\sqrt{2}$$\times$$\sqrt{2}R45^{\circ }$ surface reconstruction and electronic structure of BaSnO${}_3$ film
• Combined Spectroscopy and Electrical Characterization of La:BaSnO${}_{\text{3}}$ Thin Films and Heterostructures