Influence of oxygen pressure and aging on LaAlO3 films grown by pulsed laser deposition on SrTiO3 substrates
arXiv:1410.2492 · doi:10.1063/1.4866439
Abstract
The crystal structures of LaAlO3 films grown by pulsed laser deposition on SrTiO3 substrates at oxygen pressure of 10-3 mbar or 10-5 mbar, where kinetics of ablated species hardly depend on oxygen background pressure, are compared. Our results show that the interface between LaAlO3 and SrTiO3 is sharper when the oxygen pressure is lower. Over time, the formation of various crystalline phases is observed while the crystalline thickness of the LaAlO3 layer remains unchanged. X-ray scattering as well as atomic force microscopy measurements indicate three-dimensional growth of such phases, which appear to be fed from an amorphous capping layer present in as-grown samples.
References in corpus (14)
- Magnetic effects at the interface between nonmagnetic oxides
- Why Some Interfaces Cannot be Sharp
- Direct imaging of the coexistence of ferromagnetism and superconductivity at the LaAlO3/SrTiO3 interface
- Coexistence of Magnetic Order and Two-dimensional Superconductivity at LaAlO/SrTiO Interfaces
- The role of oxygen vacancies in SrTiO3 at the LaAlO3/SrTiO3 interface
- High Mobility in LaAlO3/SrTiO3 Heterostructures: Origin, Dimensionality and Perspectives
- Origin of charge density at LaAlO3-on-SrTiO3 hetero-interfaces; possibility of intrinsic doping
- Mapping the Spatial Distribution of Charge Carriers in LaAlO3/SrTiO3 Heterostructures
- Instability, Intermixing and Electronic Structure at the Epitaxial LaAlO3/SrTiO3(001) Heterojunction
- Evolution of the interfacial structure of LaAlO3 on SrTiO3
- Pulsed laser deposition of SrTiO3/LaGaO3 and SrTiO3/LaAlO3: plasma plume effects
- Atomic layer engineering of perovskite oxides for chemically sharp heterointerfaces
- Band offsets and density of Ti3+ states probed by X-ray photoemission on LaAlO3/SrTiO3 heterointerfaces and their LaAlO3 and SrTiO3 bulk precursors
- Electron energy loss spectroscopy determination of Ti oxidation state at the (001) LaAlO3/SrTiO3 interface as a function of LaAlO3 growth conditions