The influence of residual oxidizing impurities on the synthesis of graphene by atmospheric pressure chemical vapor deposition

Abstract

The growth of graphene on copper by atmospheric pressure chemical vapor deposition in a system free of pumping equipment is investigated. The emphasis is put on the necessity of hydrogen presence during graphene synthesis and cooling. In the absence of hydrogen during the growth step or cooling at slow rate, weak carbon coverage, consisting mostly of oxidized and amorphous carbon, is obtained on the copper catalyst. The oxidation originates from the inevitable occurrence of residual oxidizing impurities in the reactor's atmosphere. Graphene with appreciable coverage can be grown within the vacuum-free furnace only upon admitting hydrogen during the growth step. After formation, it is preserved from the destructive effect of residual oxidizing contaminants once exposure at high temperature is minimized by fast cooling or hydrogen flow. Under these conditions, micrometer-sized hexagon-shaped graphene domains of high structural quality are achieved.

Accepted in Carbon

References in corpus (7)

• The Raman Fingerprint of Graphene
• Control and Characterization of Individual Grains and Grain Boundaries in Graphene Grown by Chemical Vapor Deposition
• Graphene Segregated on Ni surfaces and Transferred to Insulators
• Raman Fingerprint of Charged Impurities in Graphene
• High Quality, Transferable Graphene Grown on Single Crystal Cu(111) Thin Films on Basal-Plane Sapphire
• Oxidation of graphene on metals
• Epitaxial (111) Films of Cu, Ni, and Cu${}_{x}Ni$_y$on\alpha -Al$_2$O$_3$(0001) for Graphene Growth by Chemical Vapor Deposition

Cited by in corpus (2)

• Do CVD grown graphene films have antibacterial activity on metallic substrates?
• Oxidation-assisted graphene heteroepitaxy on copper foil