Preparation of atomically clean and flat Si(100) surfaces by low-energy ion sputtering and low-temperature annealing

Abstract

Si(100) surfaces were prepared by wet-chemical etching followed by 0.3-1.5keV Ar ion sputtering, either at elevated or room temperature. After a brief anneal under ultrahigh vacuum conditions, the resulting surfaces were examined by scanning tunneling microscopy. We find that wet-chemical etching alone cannot produce a clean and flat Si(100) surface. However, subsequent 300eV Ar ion sputtering at room temperature followed by a 973K anneal yields atomically clean and flat Si(100) surfaces suitable for nanoscale device fabrication.

13 pages, 3 figures, to be published in Applied Surface Science

Cited by in corpus (4)

• Electrical activation and electron spin coherence of ultra low dose antimony implants in silicon
• A fabrication guide for planar silicon quantum dot heterostructures
• Direct integration of atomic precision advanced manufacturing into middle-of-line silicon fabrication
• A reduced-temperature process for preparing atomically clean Si(100) and SiGe(100) surfaces with vapor HF