Superconducting ternary compounds Li-X-B (X=Mo, W) within the mild pressure range: First-principles predictions

Abstract

Among the superconducting hydrides under high pressure, a number of studies concentrate on the ternary compounds to explore unique superconductors, which are capable of reducing the stable pressure and maintain superconductivity. In this work, to verify our proposed strategy of ternary composition lines (TCLs) to explore ternary compounds, we combined the first-principles calculations and crystal structure predictions to study the ternary compounds Li-X-B (X=Mo, W) under high pressure. After calculations along five and four TCLs in Li-W-B and Li-Mo-B, respectively, five Li-W-B compounds and four Li-Mo-B compounds were predicted. The compositions of LiWB4, Li4MoB2 and LiMo2B2 could be thermodynamically stable under high pressure, and Li2WB6 is around 0.02 eV/atom above the convex hull at 0 GPa, which has potential for synthesizing. Both of the predicted Li2WB6 P6/mmm and Li2WB4 R-3m are superconducting and their Tc are around 11 K, which are similar to the Tc of WB2 P6/mmm around 100 GPa. An anomalous increase of Tc was found in Li4MoB2 C2/m upon compression. We carried out full ternary search (FTS) to evaluate the validity of the TCLs strategy in Li-W-B system at 0 GPa. Our results are helpful for understanding the phase diagram of Li-X-B (X=Mo, W) under high pressure and the introducing of Li atoms provide candidate structures to reduce the measured stable pressure from ~100 GPa in WB2 P6/mmm to 0 GPa. Meanwhile, we preliminary validate the strategy of TCLs in structure predictions and we expect to improve this strategy in the future, shedding light on the studies of ternary compounds.

30 pages,11 figures

References in corpus (13)

• Quantum ESPRESSO: a modular and open-source software project for quantum simulations of materials
• Superconductive "sodalite"-like clathrate calcium hydride at high pressures
• Pressure-induced decomposition of solid hydrogen sulfide
• Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures
• Efficient route to achieve superconductivity improvement via substitutional La-Ce alloy superhydride at high pressure
• Phonon-mediated high-temperature superconductivity in ternary borohydride KB${}_2$H${}_8$ around 12 GPa
• Designing High-Tc Superconductors with BCS-inspired Screening, Density Functional Theory and Deep-learning
• Prediction of superconducting properties of CaB2 using anisotropic Eliashberg theory
• Creating superconductivity in WB2 through pressure-induced metastable planar defects
• Synthesis and Superconductivity in yttrium superhydrides under high pressure
• Prediction of high-Tc superconductivity in ternary actinium beryllium hydrides at low pressure
• Pressure induced superconductivity in WB2 and ReB2 through modifying the B layers
• Ternary superconducting hydrides in the La-Mg-H system