Creating superconductivity in WB2 through pressure-induced metastable planar defects
arXiv:2109.11521 · doi:10.1038/s41467-022-35191-8
Abstract
High-pressure electrical resistivity measurements reveal that the mechanical deformation of ultra-hard WB2 during compression induces superconductivity above 50 GPa with a maximum superconducting critical temperature, Tc of 17 K at 90 GPa. Upon further compression up to 190 GPa, the Tc gradually decreases. Theoretical calculations show that electron-phonon mediated superconductivity originates from the formation of metastable stacking faults and twin boundaries that exhibit a local structure resembling MgB2} (hP3, space group 191, prototype AlB2). Synchrotron x-ray diffraction measurements up to 145 GPa} show that the ambient pressure hP12 structure (space group 194, prototype WB2) continues to persist to this pressure, consistent with the formation of the planar defects above 50 GPa. The abrupt appearance of superconductivity under pressure does not coincide with a structural transition but instead with the formation and percolation of mechanically-induced stacking faults and twin boundaries. The results identify an alternate route for designing superconducting materials.
10 pages, 4 figures plus supplemental material with 9 figures
References in corpus (7)
- Quantum ESPRESSO: a modular and open-source software project for quantum simulations of materials
- Restoring the density-gradient expansion for exchange in solids and surfaces
- Generalized gradient approximation for solids and their surfaces
- Advanced capabilities for materials modelling with Quantum ESPRESSO
- Quantum ESPRESSO toward the exascale
- Towards high-throughput superconductor discovery via machine learning
- Improved tetrahedron method for the Brillouin-zone integration applicable to response functions
Cited by in corpus (13)
- Pressure-induced Superconductivity at 32 K in MoB2
- High-throughput screening for boride superconductors
- Superconductivity up to 14.2 K in MnB under pressure
- Quantifying the nonadiabaticity strength constant in recently discovered highly-compressed superconductors
- A-15 type superconducting hydride : Nanograined structure with low strain, strong electron-phonon interaction, and moderate level of nonadiabaticity
- -wave superconductivity as a model for diborides apart MgB
- Diboride compounds doped with transition metals$\unicode{x2013}$a route to superconductivity through structure stabilization as well as defects
- Nb-substitution suppresses the superconducting critical temperature of pressurized MoB
- Pressure-induced superconductivity in LaP2 with graphenelike phosphorus layer
- Super-hard and superconducting boron clathrates in the prediction of U-B compounds
- Pressure induced evolution of anisotropic superconductivity and Fermi surface nesting in a ternary boride
- Superconducting ternary compounds Li-X-B (X=Mo, W) within the mild pressure range: First-principles predictions
- Superconductivity in WBe2