Prediction of high-Tc superconductivity in ternary actinium beryllium hydrides at low pressure

Abstract

Hydrogen-rich superconductors are promising candidates to achieve room-temperature superconductivity. However, the extreme pressures needed to stabilize these structures significantly limit their practical applications. An effective strategy to reduce the external pressure is to add a light element M that binds with H to form MHx units, acting as a chemical precompressor. We exemplify this idea by performing ab initio calculations of the Ac-Be-H phase diagram, proving that the metallization pressure of Ac-H binaries, for which critical temperatures as high as 200 K were predicted at 200 GPa, can be significantly reduced via beryllium incorporation. We identify three thermodynamically stable (AcBe2H10, AcBeH8, and AcBe2H14) and four metastable compounds (fcc AcBeH8, AcBeH10, AcBeH12 and AcBe2H16). All of them are superconductors. In particular, fcc AcBeH8 remains dynamically stable down to 10 GPa, where it exhibits a superconducting transition temperature Tc of 181 K. The Be-H bonds are responsible for the exceptional properties of these ternary compounds and allow them to remain dynamically stable close to ambient pressure. Our results suggest that high-Tc superconductivity in hydrides is achievable at low pressure and may stimulate experimental synthesis of ternary hydrides.

References in corpus (29)

• Quantum ESPRESSO: a modular and open-source software project for quantum simulations of materials
• CALYPSO: a method for crystal structure prediction
• Crystal Structure Prediction via Particle Swarm Optimization
• Conventional superconductivity at 203 K at high pressures
• Superconductivity at 250 K in lanthanum hydride under high pressures
• Evidence for superconductivity above 260 K in lanthanum superhydride at megabar pressures
• Synthesis of clathrate cerium superhydride CeH9 below 100 GPa with atomic hydrogen sublattice
• Superconductive "sodalite"-like clathrate calcium hydride at high pressures
• The metallization and superconductivity of dense hydrogen sulfide
• A Perspective on Conventional High-Temperature Superconductors at High Pressure: Methods and Materials
• Anomalous high-temperature superconductivity in YH${}_6$
• Superconductivity at 253 K in lanthanum-yttrium ternary hydrides
• Superconductivity above 200 K Observed in Superhydrides of Calcium
• High-Temperature Superconductivity in Cerium Superhydrides
• Superconductivity to 262 kelvin via catalyzed hydrogenation of yttrium at high pressures
• LaBH${}_8$: the first high-T${}_c$ low-pressure superhydride
• High-Temperature Superconductivity in Alkaline and Rare Earth Polyhydrides at High Pressure: A Theoretical Perspective
• Hydrogen "penta-graphene-like" structure stabilized by hafnium: a high-temperature conventional superconductor
• Prediction of high-Tc superconductivity in ternary lanthanum borohydrides
• Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures
• Actinium hydrides $Ac{H}_{10}$, $Ac{H}_{12}$, $Ac{H}_{16}$ as high-temperature conventional superconductors
• A Symmetry-orientated Divide-and-Conquer Method for Crystal Structure Prediction
• Efficient route to achieve superconductivity improvement via substitutional La-Ce alloy superhydride at high pressure
• Phonon-mediated high-temperature superconductivity in ternary borohydride KB${}_2$H${}_8$ around 12 GPa
• In-silico synthesis of lowest-pressure high-$T_{\text{c}}$ ternary superhydrides
• Effect of paramagnetic impurities on superconductivity in polyhydrides: $\text{s}$-wave order parameter in Nd-doped LaH${}_{10}$
• From LaH10 to room-temperature superconductors
• Potential high-$T_c$ superconductivity in YCeH${}_x$ and LaCeH${}_x$ under pressure
• Superconductivity in CeBeH${}_8$ and CeBH${}_8$ at moderate pressures

Cited by in corpus (5)

• Prediction of high-Tc superconductivity under submegabar pressure in ternary actinium borohydrides
• A-15 type superconducting hydride $L{a}_4{H}_{23}$: Nanograined structure with low strain, strong electron-phonon interaction, and moderate level of nonadiabaticity
• Theoretical prediction of strong-coupling superconductivity in a hypothetical NaAlH3 phase at ambient pressure
• Superconducting ternary compounds Li-X-B (X=Mo, W) within the mild pressure range: First-principles predictions
• Composition-Based Machine Learning for Screening Superconducting Ternary Hydrides from a Curated Dataset