Microwave Performance of all MOCVD-grown AlScN/GaN MIS-HEMTs on Semi-Insulating GaN Substrates

Abstract

We report on the design, fabrication, and characterization of all MOCVD-grown long-gate AlScN/GaN metal-insulator-semiconductor high electron mobility transistors (MIS-HEMTs) on semi-insulating GaN substrates. Devices with a gate length of $1\mu$m and gate-drain spacing of $0.9\mu$ m exhibit a maximum drain current density of 1 A/mm, an on/off current ratio of $2\times 10^5$, and a three-terminal breakdown voltage of 63 V. The device has near-ideal subthreshold characteristics with a subthreshold swing of 63 mV/dec and a current dispersion as low as 7.8$\%$ at 10 V due to the excellent interfacial quality with a trap density ($D_{\mathrm{it}}$) of $2.11\times {10}^{11}{\mathrm{cm}}^{-2}e{V}^{-1}$ and the semi-insulating GaN substrate with a low threading dislocation density. Small-signal RF measurements reveal an $f_{\mathrm{T}}/f_{\max }$ of 25.8/51.1 GHz, while large-signal load-pull characterization at 10 GHz demonstrates an output power density of 4.04 W/mm with a power-added efficiency of 22.7$\%$. In addition, a minimum noise figure below 2.5 dB was measured over a wide drain current range from 100 mA/mm to 700 mA/mm below 6 GHz. These results extend previous demonstrations of short-gate MOCVD-grown AlScN/GaN HEMTs to the long-gate, high-voltage regime, confirming the robustness of this material system for both high-frequency and high-power device applications with favorable microwave noise performance.