1/ f noise and two-level systems in MBE-grown Al thin films

Abstract

Aluminum thin films are essential to the functionalities of electronic and quantum devices, where two-level systems (TLS) can degrade device performance. MBE-grown Al films may appeal to these applications due to their low TLS densities. We studied the energy distributions of TLS densities, g(E), in 10-nm-thick MBE-grown and electron-beam evaporated Al films through 1/f noise measurements between 80 and 360 K. At 300 K, the noise magnitudes in MBE-grown films are about three times lower than in the electron-beam evaporated films, corresponding to the g(E) values about ten times lower in the former than in the latter. Compared with previously established observations, we identified that the 1/f noise was generated by thermally activated TLS at grain boundaries.

arXiv comment6 pages, 5 figures

References in corpus (14)

• 1/f noise: implications for solid-state quantum information
• New material platform for superconducting transmon qubits with coherence times exceeding 0.3 milliseconds
• Planar Superconducting Resonators with Internal Quality Factors above One Million
• Coherent quantum phase slip
• Materials loss measurements using superconducting microwave resonators
• Granular aluminum: A superconducting material for high impedance quantum circuits
• High Kinetic Inductance NbN Nanowire Superinductors
• Suppression of 1/f noise in solid state quantum devices by surface spin desorption
• Substrate surface engineering for high-quality silicon/aluminum superconducting resonators
• A metastable superconducting qubit
• Ultralow 1/f Noise in a Heterostructure of Superconducting Epitaxial Cobalt-Disilicide Thin Film on Silicon
• Probing nanocrystalline grain dynamics in nanodevices
• Activation energy distribution of dynamical structural defects in RuO${}_2$ films
• Quantum-interference origin and magnitude of 1/$f$ noise in Dirac nodal line IrO${}_2$ nanowires at low temperatures