Composition variations in Cu(In,Ga)(S,Se)2 solar cells: not a gradient, but an interlaced network of two phases

Abstract

Record efficiency in chalcopyrite-based solar cells Cu(In,Ga)(S,Se)2 is achieved using a gallium gradient to increase the band gap of the absorber towards the back side. Although this structure has successfully reduced recombination at the back contact, we demonstrate that in industrial absorbers grown in the pilot line of Avancis, the back part is a source of non-radiative recombination. Depth-resolved photoluminescence (PL) measurements reveal two main radiative recombination paths at 1.04 eV and 1.5-1.6 eV, attributed to two phases of low and high band gap material, respectively. Instead of a continuous change in the band gap throughout the thickness of the absorber, we propose a model where discrete band gap phases interlace, creating an apparent gradient. Cathodoluminescence and Raman scattering spectroscopy confirm this result. Additionally, deep defects associated to the high gap phase reduce the absorber performance. Etching away the back part of the absorber leads to an increase of one order of magnitude in the PL intensity, i.e., 60 meV in quasi Fermi level splitting. Non-radiative voltage losses correlate linearly with the relative contribution of the high energy PL peak, suggesting that reducing the high gap phase could increase the open circuit voltage by up to 180 mV.

References in corpus (1)

• Solar cell efficiency, diode factor and interface recombination: insights from photoluminescence

Cited by in corpus (4)

• Improved sequentially processed Cu(In,Ga)(S,Se)2 by Ag alloying
• The effect of a band gap gradient on the radiative losses in the open circuit voltage of solar cells
• Sodium induced beneficial effects in wide bandgap Cu(In,Ga)S2 solar cell with 15.7% efficiency
• Silver Alloyed Wide Bandgap (Ag,Cu)(In,Ga)S2 Thin Film Solar Cells With 15.5% Efficiency