Interface recombination in Ga- and N-polar GaN/(Al,Ga)N quantum wells grown by molecular beam epitaxy

Abstract

We explore and systematically compare the morphological, structural and optical properties of GaN/(Al,Ga)N multiple quantum wells (MQWs) grown by plasma-assisted molecular beam epitaxy (PA-MBE) on freestanding GaN$(0001)$ and GaN$(000\bar{1})$ substrates. Samples of different polarity are found to be comparable in terms of their morphological and structural perfection and exhibit essentially identical quantum well widths and Al content. Regardless of the crystal orientation, the exciton decay in the MQWs at 10 K is dominantly radiative and the photoluminescence (PL) energy follows the quantum confined Stark effect (QCSE) for different quantum well widths. A prominent free-to-bound transition involving interface shallow donors is, however, visible for the N-polar MQWs. At room-temperature, in contrast, the exciton decay in all samples is dominated by nonradiative recombination taking place at point defects, presumably Ca or V N located at the bottom QW interface. Remarkably, the N-polar MQWs exhibit a higher PL intensity and longer decay times than the Ga-polar MQWs at room-temperature. This improved internal quantum efficiency is attributed to the beneficial orientation of the internal electric field that effectively reduces the capture rate of minority carriers by interface trap states.

References in corpus (5)

• Correct implementation of polarization constants in wurtzite materials and impact on III-nitrides
• Impact of Residual Carbon Impurities and Gallium Vacancies on Trapping Effects in AlGaN/GaN MIS-HEMTs
• High conductivity Polarization-induced 2D hole gases in Undoped GaN/AlN Heterojunctions enabled by Impurity Blocking Layers
• Comparison of the luminous efficiency of Ga- and N-polar In${}_x$Ga${}_{1-x}$N/In${}_y$Ga${}_{1-y}$N quantum wells grown by plasma-assisted molecular beam epitaxy
• Luminescent N-polar (In,Ga)N/GaN quantum wells grown by plasma-assisted molecular beam epitaxy at high temperature

Cited by in corpus (1)

• Excitonic and deep-level emission from N- and Al-polar homoepitaxial AlN grown by molecular beam epitaxy