Fabrication of small superconducting coils using (Ba,A)Fe2As2 (A: Na, K) round wires with large critical current densities

Abstract

We report the fabrication of small (Ba,A)Fe2As2 (A: Na, K) coils using 10 m-class long round wires, fabricated by powder-in-tube (PIT) method. Coils are sintered using hot-isostatic-press (HIP) technique after glass-fiber insulations are installed. Critical current (Ic) of the whole coil using (Ba,Na)Fe2As2 and (Ba,K)Fe2As2 are 60 A and 66 A under the self-field, and the generated magnetic fields at the center of the coil reach 2.6 kOe and 2.5 kOe, respectively. Furthermore, the largest transport critical current density (Jc) and Ic in (Ba,Na)Fe2As2 wires picked up from the coil reach 54 kAcm-2 and 51.8 A at T = 4.2 K under a magnetic field of 100 kOe, respectively. This value exceeds transport Jc of all previous iron-based superconducting round wires. Texturing of grains in the core of the wire due to the improvement of the wire drawing process plays a key role for the enhancement of Jc.

arXiv comment25 pages, 1 table, 9 figures, accepted in Superconductor Science and Technology

References in corpus (24)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity up to 37 K in (A1-xSrx)Fe2As2 with A=K and Cs
• Nearly Isotropic superconductivity in (Ba,K)Fe2As2
• Recent advances in iron-based superconductors toward applications
• Exploration of new superconductors and functional materials and fabrication of superconducting tapes and wires of iron pnictides
• Advantageous grain boundaries in iron pnictide superconductors
• High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
• Progress in wire fabrication of iron-based superconductors
• Determination of anisotropic Hc2 up to 60 T in (Ba0.55K0.45)Fe2As2 single crystals
• Enhancement of Critical Current Densities in Co-Doped BaFe${}_2$As${}_2$ with Columnar Defects Introduced by Heavy-Ion Irradiation
• Very strong intrinsic supercurrent carrying ability and vortex avalanches in (Ba,K)Fe2As2 superconducting single crystals
• Realization of practical level current densities in Sr0.6K0.4Fe2As2 tape conductors for high-field applications
• High transport current superconductivity in powder-in-tube Ba0.6K0.4Fe2As2 tapes at 27 tesla
• Structural, Magnetic, and Superconducting Properties of Ba1-xNaxFe2As2
• Hot pressing to enhance the transport Jc of Sr0.6K0.4Fe2As2 superconducting tapes
• Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils
• Enhancement of critical current densities in (Ba,K)Fe2As2 wires and tapes using HIP technique
• First performance test of 30 mm iron-based superconductor single pancake coil under 24 T background field
• High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process
• Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes
• Fabrication and transport properties of Sr0.6K0.4Fe2As2 multifilamentary superconducting wires
• Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors
• Enhancement of critical current density in (Ba,Na)Fe2As2 round wires using high-pressure sintering
• Enhancement of Critical Current Densities in (Ba,K)Fe2As2 by 320 MeV Au Irradiation in Single Crystals and by High-Pressure Sintering in PIT Wires