High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

Abstract

The recently discovered iron-based superconductors with very high upper critical field and small anisotropy have been regarded as a potential candidate material for high field applications. However, enhancements of superconducting properties are still needed to boost the successful use of iron-based superconductors in such applications. Here, we propose a new sheath architecture of stainless steel (SS)/Ag double sheath and investigate its influence on the microstructures and Jc-H property. We found that the transport Jc-H curves for rolled and pressed tapes both show extremely small magnetic field dependence and exceed 3*10^4A/cm^2 under 28 T, which are much higher than those of low-temperature superconductors. More interestingly, 12 cm long rolled tape shows very high homogeneity and sustains Jc as high as 7.7*10^4 A/cm^2 at 10 T. These are the highest values reported so far for iron-based superconducting wires fabricated by scalable rolling process. The microstructure investigations indicate that such high Jc was achieved by higher density of the core and uniform deformation resulting better texturing. These results indicate that our process is very promising for fabricating long Ba122 wires for high field magnet, i.e. above 20 T.

arXiv comment19 pages, 6 figures

References in corpus (16)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity at 43 K in Samarium-arsenide Oxides $SmFeAs{O}_{1-x}{F}_x$
• Nearly Isotropic superconductivity in (Ba,K)Fe2As2
• Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
• New Fe-based superconductors: properties relevant for applications
• Advantageous grain boundaries in iron pnictide superconductors
• High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
• The behavior of grain boundaries in the Fe-based superconductors
• Realization of practical level current densities in Sr0.6K0.4Fe2As2 tape conductors for high-field applications
• Fabrication of the iron-based superconducting wire using Fe(Se, Te)
• Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
• Strong vortex pinning in Co-doped BaFe2As2 single crystal thin films
• Superconductivity of powder-in-tube Sr0.6K0.4Fe2As2 wires
• High transport critical current densities in textured Fe-sheathed Sr1-xKxFe2As2+Sn superconducting tapes
• Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method
• Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

Cited by in corpus (10)

• Recent advances in iron-based superconductors toward applications
• Exploration of new superconductors and functional materials and fabrication of superconducting tapes and wires of iron pnictides
• Doping-dependent critical current properties in K, Co, and P-doped BaFe2As2 single crystals
• Plastic pinning replaces collective pinning as the second magnetization peak disappears in the pnictide superconductor Ba-KFe${}_2$As${}_2$
• Fabrication of small superconducting coils using (Ba,A)Fe2As2 (A: Na, K) round wires with large critical current densities
• Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors
• Synthesis of CaKFe${}_4$As${}_4$ bulk samples with high critical current density using a spark plasma sintering technique
• Large transport Jc in Cu-sheathed Sr0.6K0.4Fe2As2 superconducting tape conductors
• Strengthened proximity effect at grain boundaries to enhance inter-grain supercurrent in Ba1-xKxFe2As2 superconductors
• Crystal structure instability of FeSe grains: Formation of non-superconducting phase at the grain surface