Superconductivity in Undoped BaFe2As2 by Tetrahedral Geometry Design
arXiv:2001.00277 · doi:10.1073/pnas.2001123117
Abstract
Fe-based superconductors exhibit a diverse interplay between charge, orbital, and magnetic ordering1-4. Variations in atomic geometry affect electron hopping between Fe atoms5,6 and the Fermi surface topology, influencing magnetic frustration and the pairing mechanism through changes of orbital overlap and occupancies7-11. Here, we experimentally demonstrate a systematic approach to realize superconductivity without chemical doping in BaFe2As2, employing geometric design within an epitaxial heterostructure. We control both tetragonality and orthorhombicity in BaFe2As2 through superlattice engineering, which we experimentally find to induce superconductivity when the As-Fe-As bond angle approaches that in a regular tetrahedron. This approach of superlattice design could lead to insights into low dimensional superconductivity in Fe-based superconductors.
References in corpus (13)
- Magnetic Order versus superconductivity in the Iron-based layered La(O1-xFx)FeAs systems
- High-temperature superconductivity in iron-based materials
- Superconductivity in single-layer films of FeSe with a transition temperature above 100 K
- Spin density wave anomaly at 140 K in the ternary iron arsenide BaFe2As2
- Evidence for an electron nematic phase transition in underdoped iron pnictide superconductors
- Effect of Structural Parameters on Superconductivity in Fluorine-Free LnFeAsO1-y (Ln=La,Nd)
- Highly crystalline 2D superconductors
- High-temperature interface superconductivity between metallic and insulating cuprates
- Observation of Lattice and Andreev Bound States of Vortices in Ba0.6K0.4Fe2As2 Single Crystals with Scanning Tunneling Microscopy/Spectroscopy
- Resistivity and upper critical field in KFeAs single crystals
- The cleavage surface of the BaFe_(2-x)Co_(x)As_(2) and Fe_(y)Se_(1-x)Te_(x) superconductors: from diversity to simplicity
- Water-induced superconductivity in SrFe2As2
- Heat capacity study of BaFeAs: effects of annealing