arXiv:1804.09998 · doi:10.1021/acsnano.5b03220

Abstract

This article addresses the much debated question whether the degree of hydrophobicity of single-layer graphene (1LG) is different from the one of double-layer graphene (2LG). Knowledge of the water affinity of graphene and its spatial variations is critically important as it can affect the graphene properties as well as the performance of graphene devices exposed to humidity. By employing chemical force microscopy (CFM) with a probe rendered hydrophobic by functionalization with octadecyltrichlorosilane (OTS), the adhesion force between the probe and epitaxial graphene on SiC has been measured in deionized water. Owing to the hydrophobic attraction, a larger adhesion force was measured on 2LG domains of graphene surfaces, thus showing that 2LG is more hydrophobic than 1LG. Identification of 1LG and 2LG domains was achieved through Kelvin probe force microscopy and Raman spectral mapping. Approximate values of the adhesion force per OTS molecule have been calculated through contact area analysis. Furthermore, the contrast of friction force images measured in contact mode was reversed to the 1LG/2LG adhesion contrast and its origin was discussed in terms of the likely water depletion over hydrophobic domains as well as deformation in the contact area between AFM tip and 1LG.

arXiv commentThis document is the unedited Author's version of a Submitted Work that was subsequently accepted for publication in ACS Nano ©American Chemical Society after peer review. To access the final edited and published work see URL: https://pubs.acs.org/doi/abs/10.1021/acsnano.5b03220

References in corpus (8)

Cited by in corpus (11)