Epitaxial Heusler Superlattice Co2MnAl/Fe2MnAl with Perpendicular Magnetic Anisotropy and Termination-Dependent Half-Metallicity

Abstract

Single-crystal Heusler atomic-scale superlattices that have been predicted to exhibit perpendicular magnetic anisotropy and half-metallicity have been successfully grown by molecular beam epitaxy. Superlattices consisting of full-Heusler Co${}_2$MnAl and Fe${}_2$MnAl with one to three unit cell periodicity were grown on GaAs (001), MgO (001), and Cr (001)/MgO (001). Electron energy loss spectroscopy maps confirmed clearly segregated epitaxial Heusler layers with high cobalt or high iron concentrations for samples grown near room temperature on GaAs (001). Superlattice structures grown with an excess of aluminum had significantly lower thin film shape anisotropy and resulted in an out-of-plane spin reorientation transition at temperatures below 200 K for samples grown on GaAs (001). Synchrotron-based spin resolved photoemission spectroscopy found that the superlattice structure improves the Fermi level spin polarization near the X point in the bulk Brillouin zone. Stoichiometric Co${}_2$MnAl terminated superlattice grown on MgO (001) had a spin polarization of 95%, while a pure Co${}_2$MnAl film had a spin polarization of only 65%.

arXiv comment14 pages, 1 table, 6 figures

References in corpus (6)

• High spin polarization of the anomalous Hall current in Co-based Heusler compounds
• Direct evidence for minority spin gap in the Co2MnSi Heusler alloy
• Doping and disorder in the Co${}_2$MnAl and Co${}_2$MnGa half-metallic Heusler alloys
• Observation of a topologically non-trivial surface state in half-Heusler PtLuSb (001) thin films
• Designing a fully-compensated half-metallic ferrimagnet
• Exchange coupling of a perpendicular ferromagnet to a half-metallic compensated ferrimagnet via a thin hafnium interlayer

Cited by in corpus (1)

• Perspective: Heusler interfaces -- opportunities beyond spintronics?