Strongly connected ex-situ MgB2 polycrystalline bulks fabricated by solid-state self-sintering

Abstract

We have investigated the microstructure, normal-state electrical connectivity, and critical current density of ex-situ MgB2 polycrystalline bulks prepared by systematically varying the sintering conditions under low pressure. Samples heated at a high temperature of ~900°C for a long period showed an increased packing factor, a larger intergrain contact area, and a significantly enhanced electrical connectivity, all of which indicate solid-state self-sintering of MgB2. Sintered ex-situ MgB2 bulks from a laboratory-made ball-milled powder exhibited a greatly enhanced connectivity of 28%, which is the highest connectivity of pressureless ex-situ MgB2 bulks, wires, and tapes. Surprisingly, grain growth did not occur during long-duration (~100 h) sintering in the sintered ex-situ MgB2 bulks. This is in marked contrast to in-situ processed MgB2 samples for which significant grain growth occurred during heat treatment at ~900°C, producing grains that are several tens of times larger than the initial boron grains. Consequently, the critical current density as a function of the external magnetic field at 20 K progressively improved with sintering due to the relatively small grain size and good intergrain connectivity. We thus conclude that solid-state self-sintering is an effective approach for producing strongly connected, dense ex-situ MgB2 polycrystals without grain growth.

21 pages, 9 figures, to be published in Supercond. Sci. Technol

References in corpus (9)

• Strongly linked current flow in polycrystalline forms of the new superconductor MgB2
• Large transport critical currents in unsintered MgB2 superconducting tapes
• Thermodynamics of the Mg-B system: Implications for the deposition of MgB2 thin films
• Prospects for Improving the Intrinsic and Extrinsic Properties of Magnesium Diboride Superconducting Strands
• Universal relationship between crystallinity and irreversibility field of MgB2
• Nanoscale grains, high irreversibility field, and large critical current density as a function of high energy ball milling time in C-doped magnesium diboride
• Transport - and inductive critical current densities in superconducting MgB2
• Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
• Towards the Realization of Higher Connectivity in MgB2 Conductors: In-situ or Sintered Ex-situ?

Cited by in corpus (2)

• High temperature heat treatment of B precursor and P.I.T. process optimization to increase Jc performances of MgB2-based conductor
• Microwave Response of Coaxial Cavities Made of Bulk Magnesium Diboride