High temperature heat treatment of B precursor and P.I.T. process optimization to increase Jc performances of MgB2-based conductor

arXiv:1405.4099 · doi:10.1088/0953-2048/26/10/105022

Abstract

Promising results reported in our previous works led us to think that production of B powder plays a crucial role in MgB2 synthesis. A new method for boron preparation has been developed in our laboratory. This particular process is based on magnesiothermic reaction (Moissan process) with the addition of an initial step that gives boron powder with nano-metric grain size. In this paper we report our efforts regarding optimization of PIT method for these nanometric powders and the resolution of problems previously highlighted such as the difficulty in powder packaging and the high friction phenomena occurring during cold working. This increases cracking during the tape and wire manufacturing leading to its failure. Packaging problems are related to the amorphous nature of boron synthesized in our laboratory, so a crystallization treatment was applied to improve crystallinity of B powder. To prevent excessive friction phenomena we synthesized non-stoichiometric MgB2 and using magnesium as lubricant. Our goal is the Jc improvement, but a global physical-chemical characterization was also made to analyze the improvement given by our treatments: this characterization includes X-ray diffraction, resistivity vs. temperature measurement, SEM image, besides magnetic and transport Jc measurements.

arXiv comment15 pages, 11 figures

References in corpus (10)

Cited by in corpus (1)