Residual disorder and diffusion in thin Heusler alloy films
arXiv:1206.2242 · doi:10.1103/PhysRevB.86.075319
Abstract
Co2FeSi/GaAs(110) and Co2FeSi/GaAs(111)B hybrid structures were grown by molecular-beam epitaxy and characterized by transmission electron microscopy (TEM) and X-ray diffraction. The films contained inhomogeneous distributions of ordered L2_1 and B2 phases. The average stoichiometry was controlled by lattice parameter measurements, however diffusion processes lead to inhomogeneities of the atomic concentrations and the degradation of the interface, influencing long-range order. An average long-range order of 30-60% was measured by grazing-incidence X-ray diffraction, i.e. the as-grown Co2FeSi films were highly but not fully ordered. Lateral inhomogeneities of the spatial distribution of long-range order in Co2FeSi were found using dark-field TEM images taken with superlattice reflections.
References in corpus (7)
- Spintronics: Fundamentals and applications
- Geometric, electronic, and magnetic structure of CoFeSi: Curie temperature and magnetic moment measurements and calculations
- Investigation of CoFeSi: The Heusler compound with Highest Curie Temperature and Magnetic Moment
- A spin metal-oxide-semiconductor field-effect transistor using half-metallic-ferromagnet contacts for the source and drain
- Analysis of L21-ordering in full-Heusler Co2FeSi alloy thin films formed by rapid thermal annealing
- Structure and magnetism of self-organized Ge(1-x)Mn(x) nano-columns
- Electric-field control of spin accumulation signals in silicon at room temperature