Evidence for electromagnetic granularity in polycrystalline Sm1111 iron-pnictides with enhanced phase purity

Abstract

We prepared polycrystalline SmFeAsO1-xFx (Sm1111) bulk samples by sintering and hot isostatic pressing (HIP) in order to study the effects of phase purity and relative density on the intergranular current density. Sintered and HIPped Sm1111 samples are denser with fewer impurity phases, such as SmOF and the grain boundary wetting phase, FeAs. We found quite complex magnetization behavior due to variations of both the inter and intragranular current densities. Removing porosity and reducing second phase content enhanced the intergranular current density, but HIPping reduced Tc and the intragranular current density, due to loss of fluorine and reduction of Tc. We believe that the HIPped samples are amongst the purest polycrystalline 1111 samples yet made. However, their intergranular current densities are still small, providing further evidence that polycrystalline pnictides, like polycrystalline cuprates, are intrinsically granular.

14 pages, 6 figures

References in corpus (14)

• Spin density wave anomaly at 140 K in the ternary iron arsenide BaFe2As2
• The superconductivity at 18 K in LiFeAs system
• Nearly Isotropic superconductivity in (Ba,K)Fe2As2
• Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
• Upper critical fields and thermally-activated transport of Nd(O_0.7F_0.3)FeAs single crystal
• Upper critical fields well above 100 T for the superconductor SmFeAsO${}_{0.85}$F${}_{0.15}$ with T${}_c$ = 46 K
• Evidence for two distinct scales of current flow in polycrystalline Sm and Nd iron oxypnictides
• Fabrication of the iron-based superconducting wire using Fe(Se, Te)
• Superconducting properties of SmO1-xFxFeAs wires with Tc = 52 K prepared by the powder-in-tube method
• Intrinsic magnetic properties of NdFeAsO${}_{0.9}$F${}_{0.1}$ superconductor from local and global measurements
• Synthesis, crystal structure, microstructure, transport and magnetic properties of SmFeAsO and SmFeAs(O0.93F0.07)
• Evidence for electromagnetic granularity in the polycrystalline iron-based superconductor LaO0.89F0.11FeAs
• Combined microstructural and magneto optical study of current flow in polycrystalline forms of Nd and Sm Fe-oxypnictides
• Evidence for Supercurrent Connectivity in Conglomerate Particles in NdFeAsO1-d

Cited by in corpus (1)

• Anomalous Tail Effect on Resistivity Transition and Weak-link Behavior of Iron Based Superconductor