Simulation of mechanical effects of hydrogen in bicrystalline Cu using DFT and bond order potentials

Vasileios Fotopoulos, Alexander L. Shluger

Hydrogen embrittlement is a prime cause of several degradation effects in metals. Since grain boundaries (GBs) act efficiently as sinks for hydrogen atoms, H is thought to segregat…