A tetragonal-to-monoclinic phase transition in a ferroelectric perovskite: the structure of PbZr(0.52)Ti(0.48)O3

arXiv:cond-mat/9910066 · doi:10.1103/PhysRevB.61.8687

Abstract

The perovskite-like ferroelectric system PbZr(1-x)Ti(x)O3 (PZT) has a nearly vertical morphotropic phase boundary (MPB) around x=0.45-0.50. Recent synchrotron x-ray powder diffraction measurements by Noheda et al. [Appl. Phys. Lett. 74, 2059 (1999)] have revealed a new monoclinic phase between the previously-established tetragonal and rhombohedral regions. In the present work we describe a Rietveld analysis of the detailed structure of the tetragonal and monoclinic PZT phases on a sample with x= 0.48 for which the lattice parameters are respectively: at= 4.044 A, ct= 4.138 A, at 325 K, and am= 5.721 A, bm= 5.708 A, cm= 4.138 A, beta= 90.496 deg., at 20K. In the tetragonal phase the shifts of the atoms along the polar [001] direction are similar to those in PbTiO3 but the refinement indicates that there are, in addition, local disordered shifts of the Pb atoms of ~0.2 A perpendicular to the polar axis.. The monoclinic structure can be viewed as a condensation along one of the <110> directions of the local displacements present in the tetragonal phase. It equally well corresponds to a freezing-out of the local displacements along one of the <100> directions recently reported by Corker et al.[J. Phys. Condens. Matter 10, 6251 (1998)] for rhombohedral PZT. The monoclinic structure therefore provides a microscopic picture of the MPB region in which one of the "locally" monoclinic phases in the "average" rhombohedral or tetragonal structures freezes out, and thus represents a bridge between these two phases.

REVTeX, 7 figures. Modifications after referee's suggestion: new figure (figure 5), comments in 2nd para. (Sect.III) and in 2nd & 3rd para. (Sect. IV-a), in the abstract: "...of ~0.2 A perpendicular to the polar axis."

References in corpus (7)

Cited by in corpus (61)