Reversing Hydrogen-Related Loss in $\alpha$-Ta Thin Films for Quantum Device Fabrication

Abstract

$\alpha$-Tantalum ($\alpha$-Ta) is an emerging material for superconducting qubit fabrication due to the low microwave loss of its stable native oxide. However, hydrogen absorption during fabrication, particularly when removing the native oxide, can degrade performance by increasing microwave loss. In this work, we demonstrate that hydrogen can enter $\alpha$-Ta thin films when exposed to 10 vol% hydrofluoric acid for 3 minutes or longer, leading to an increase in power-independent ohmic loss in high-Q resonators at millikelvin temperatures. Reduced resonator performance is likely caused by the formation of non-superconducting tantalum hydride (TaH${}_x$) precipitates. We further show that annealing at 500°C in ultra-high vacuum (10${}^{-8}$ Torr) for one hour fully removes hydrogen and restores the resonators' intrinsic quality factors to ~4 million at the single-photon level. These findings identify a previously unreported loss mechanism in $\alpha$-Ta and offer a pathway to reverse hydrogen-induced degradation in quantum devices based on Ta and, by extension also Nb, enabling more robust fabrication processes for superconducting qubits.

11 pages, 5 figures

References in corpus (13)

• Systematic Improvements in Transmon Qubit Coherence Enabled by Niobium Surface Encapsulation
• Identifying optimal cycles in quantum thermal machines with reinforcement-learning
• Investigation of microwave loss induced by oxide regrowth in high-Q Nb resonators
• Proximity breakdown of hydrides in superconducting niobium cavities
• High-coherence superconducting qubits made using industry-standard, advanced semiconductor manufacturing
• Chemical profiles of the oxides on tantalum in state of the art superconducting circuits
• High-kinetic inductance NbN films for high-quality compact superconducting resonators
• Superconductivity Observed in Tantalum Polyhydride at High Pressure
• Formation and Microwave Losses of Hydrides in Superconducting Niobium Thin Films Resulting from Fluoride Chemical Processing
• Quantifying quantum coherence of multiple-charge states in tunable Josephson junctions
• Manufacturing high-Q superconducting α-tantalum resonators on silicon wafers
• Low-Loss Superconducting Resonators Fabricated from Tantalum Films Grown at Room Temperature
• Annealing reduces Si${}_3$N${}_4$ microwave-frequency dielectric loss in superconducting resonators

Cited by in corpus (2)

• Investigation of tantalum films growth for coplanar resonators with internal quality factors above ten million
• Enhanced Tantalum Superconducting Resonator Performance via All-Surface Organic Monolayer Passivation