Hydride Units Filled B--C Clathrate: A New Pathway for High-Temperature Superconductivity at Ambient Pressure
arXiv:2311.01656 · doi:10.1038/s42005-024-01814-3
Abstract
The pursuit of room-temperature superconductors has recently advanced with the discovery of high-temperature superconductivity in compressed hydrides, although sustaining the superconductivity of hydrides at ambient pressure remains challenging. In parallel, -bonded frameworks comprising lightweight elements (\textit{e.g.}, boron and carbon) have emerged as another avenue for developing ambient-pressure superconductors. However, despite their stability at low pressures, the critical temperature () values observed in these materials have not yet reached the impressive benchmarks set by hydride-based superconductors. Here we propose a novel design strategy for achieving high-temperature superconductivity at ambient pressure by integrating hydride units into B-C clathrate structures. This approach exploits the beneficial properties of hydrogen, the lightest element, to enhance the superconductivity beyond that of the parent compounds. For instance, our computational predictions indicate that doping SrBC with ammonium (NH) yields a SrNHBC compound with an estimated of 85 K at ambient pressure -- more than double that of its precursor (31 K). Extensive substitution across the periodic table results in a family of MNHNHBC superconductors that are predicted to be superconducting at ambient pressure. These compounds can potentially be synthesized using high-pressure techniques and then quenched to ambient conditions, with the highest predicted ambient-pressure of 115 K in PbNHBC. Our findings present a promising strategy for discovering high- superconductors at ambient pressure, potentially revolutionizing technologies reliant on superconducting materials.
7 pages, 4 figures
References in corpus (27)
- Quantum ESPRESSO: a modular and open-source software project for quantum simulations of materials
- CALYPSO: a method for crystal structure prediction
- Crystal Structure Prediction via Particle Swarm Optimization
- Conventional superconductivity at 203 K at high pressures
- Superconductivity at 250 K in lanthanum hydride under high pressures
- Evidence for superconductivity above 260 K in lanthanum superhydride at megabar pressures
- Implementation strategies in phonopy and phono3py
- Superconductive "sodalite"-like clathrate calcium hydride at high pressures
- The metallization and superconductivity of dense hydrogen sulfide
- Quantum Crystal Structure in the 250 K Superconducting Lanthanum Hydride
- Superconductivity at 253 K in lanthanum-yttrium ternary hydrides
- Superconductivity above 200 K Observed in Superhydrides of Calcium
- Superconductivity to 262 kelvin via catalyzed hydrogenation of yttrium at high pressures
- Towards high-throughput superconductor discovery via machine learning
- The Stochastic Self-Consistent Harmonic Approximation: Calculating Vibrational Properties of Materials with Full Quantum and Anharmonic Effects
- Tellurium Hydrides at High Pressures: High-temperature Superconductors
- Improved tetrahedron method for the Brillouin-zone integration applicable to response functions
- Feasible route to high-temperature ambient-pressure hydride superconductivity
- Phonon-mediated high-temperature superconductivity in ternary borohydride KBH around 12 GPa
- Prediction of Ambient Pressure Conventional Superconductivity above 80K in Thermodynamically Stable Hydride Compounds
- Conventional high-temperature superconductivity in metallic, covalently bonded, binary-guest C-B clathrates
- In-silico synthesis of lowest-pressure high- ternary superhydrides
- High-T Superconductivity in doped boron-carbon clathrates
- Synthesis and Superconductivity in yttrium superhydrides under high pressure
- Breakdown of the Migdal-Eliashberg theory and a theory of lattice-fermionic superfluidity
- Quantum lattice dynamics and their importance in ternary superhydride clathrates
- Origins of low- and high-pressure discontinuities of in niobium