Evaluation of predictive correlation between flux expulsion and grain growth for superconducting radio frequency cavities

Abstract

A series of experiments were carried out in an effort to develop a simple method for predicting magnetic flux expulsion behavior of high purity niobium used to fabricate superconducting radio frequency (SRF) cavities. Using conventional metallographic characterizations in conjunction with high spatial resolution electron backscattered diffraction-orientation imaging microscopy (EBSD-OIM), we found that the flux expulsion behavior of 1.3 GHz single cell SRF Nb cavities is significantly associated with the grain growth of the Nb material during heat treatment. Most of Nb grains rapidly grew during 900C heat treatment, and likely full-recrystallized with 1000C HT. With comparison of the magnetic flux expulsion ratio (Bsc/Bnc) at dT = 5 K, the flux expulsion efficiency of the cavities increases along with increasing of grain size. Most interestingly, 900C HT shows a roughly linear trend that suggests this criterion could be used to predict appropriate heat treatment temperature for sufficient flux expulsion behavior in SRF-grade Nb. This result would be used to see if flux expulsion can be predicted by examining the materials coming from the Nb vendor, prior to cavity fabrication.

References in corpus (10)

• Nitrogen and argon doping of niobium for superconducting radio frequency cavities: a pathway to highly efficient accelerating structures
• Unprecedented Quality Factors at Accelerating Gradients up to 45 MV/m in Niobium Superconducting Resonators via Low Temperature Nitrogen Infusion
• Ultra-high quality factors in superconducting niobium cavities in ambient magnetic fields up to 190 mG
• Dependence of the residual surface resistance of superconducting RF cavities on the cooling dynamics around $T_{\mathrm{c}}$
• Dynamics of vortex penetration, jumpwise instabilities and nonlinear surface resistance of type-II superconductors in strong rf fields
• Efficient expulsion of magnetic flux in superconducting RF cavities for high $Q_0$ applications
• Ultra-Low Surface Resistance via Vacuum Heat Treatment of Superconducting Radiofrequency Cavities
• Effect of Low Temperature Baking in Nitrogen on the Performance of a Niobium Superconducting Radio Frequency Cavity
• Flux expulsion in niobium superconducting radio-frequency cavities of different purity and essential contributions to the flux sensitivity
• The Role of Magnetic Flux Expulsion to Reach Q0>3x10^10 in SRF Cryomodules