Non-charge-transfer origin of Tc Enhancement in a Surface Superconductor Si(111)-(root7xroot3)-In with Adsorbed Organic Molecules

Abstract

The effects of adsorption of Zn-phthalocyanine (ZnPc) molecules on the superconductivity of the Si(111)-(root7xroot3)-In surface are studied through transport measurements under ultrahigh vacuum environment. The ZnPc molecules are found to increase the transition temperature Tc by 11% at maximum, which is about 2.7 times the Tc increase previously reported using CuPc. By contrast, angle-resolved photoemission spectroscopy measurements and ab initio calculations show that charge transfer from the In atomic layers to ZnPc is substantially smaller than that to CuPc. This clearly shows that charge transfer should be excluded as the origin of the increase in Tc. The push-back effect induced by physical adsorption of molecules is discussed as a possible mechanism for the Tc enhancement.

References in corpus (13)

• Magic-angle graphene superlattices: a new platform for unconventional superconductivity
• Interface induced high temperature superconductivity in single unit-cell FeSe films on SrTiO3
• Superconductivity in single-layer films of FeSe with a transition temperature above 100 K
• Phase Diagram and High Temperature Superconductivity at 65 K in Tuning Carrier Concentration of Single-Layer FeSe Films
• Metallic ground state in an ion-gated two-dimensional superconductor
• Direct Observation of Superconductivity in Calcium-Intercalated Bilayer Graphene by in situ Electrical Transport Measurements
• Macroscopic Superconducting Current through a Silicon Surface Reconstruction with Indium Adatoms: Si(111)-(R7$\times$R3)-In
• Two-dimensional Superconductors with Atomic-scale Thicknesses
• Imaging Josephson Vortices on the Surface Superconductor Si(111)-(root7xroot3)-In using a Scanning Tunneling Microscope
• Realization of a hole-doped Mott insulator on a triangular silicon lattice
• New Identification of Metallic Phases of In Atomic layers on Si(111) Surfaces
• Atomic-layer Rashba-type superconductor protected by dynamic spin-momentum locking
• Hexagonal Indium Double Layer on Si(111)-($\sqrt{7}\times \sqrt{3})$