Effect of Co Substitution on Ferrimagnetic Heusler compound Mn3Ga

Abstract

Effect of Co substitution on Mn${}_3$Ga is investigated using first-principles study for structural and magnetic properties. Without Co, ferrimagnetic Heusler compound Mn3Ga is in tetragonal phase. With Co substitution, depending on Co concentration (x) Mn${}_3$Ga prefers tetragonal (cubic) phase when x \leq 0.5 (x \geq 0.5). Ferrimagnetism is robust regardless of x in both phases. While magnetic moments of two Mn do not vary significantly with x, Co magnetic moment in two phases exhibit different behaviors, leading to distinct features in total magnetic moment (M_{tot}). When x \leq 0.5, in tetragonal phase, Co magnetic moment is vanishingly small, resulting in a decrease of M_{tot} with x. In contrast, when x \geq 0.5, in cubic phase, Co magnetic moment is roughly 1${\mu }_B$, which is responsible for an increase of Mtot. Electronic structure is analyzed with partial density of states for various x. To elucidate the counterintuitively small Co moment, the magnetic exchange interaction is investigated where exchange coefficient between Co and Mn is much smaller in x \leq 0.5 case than x \geq 0.5 one.

5 pages 4 figures

References in corpus (5)

• Design of compensated ferrimagnetic Heusler alloys for giant tunable exchange bias
• Heusler 4.0: Tunable Materials
• Guidelines for understanding cubic manganese-rich Heusler compounds
• Compensated ferrimagnetic tetragonal Heusler thin films for antiferromagnetic spintronics
• Chemical disorder as engineering tool for spin-polarizationin Mn3Ga-based Heusler systems