Hydrogenated Amorphous Silicon Carbide: A Low-loss Deposited Dielectric for Microwave to Submillimeter Wave Superconducting Circuits

Abstract

Low-loss deposited dielectrics will benefit superconducting devices such as integrated superconducting spectrometers, superconducting qubits and kinetic inductance parametric amplifiers. Compared with planar structures, multi-layer structures such as microstrips are more compact and eliminate radiation loss at high frequencies. Multi-layer structures are most easily fabricated with deposited dielectrics, which typically exhibit higher dielectric loss than crystalline dielectrics. We measured the sub-kelvin and low-power microwave and mm-submm wave dielectric loss of hydrogenated amorphous silicon carbide (a-SiC:H), using a superconducting chip with NbTiN/a-SiC:H/NbTiN microstrip resonators. We deposited the a-SiC:H by plasma-enhanced chemical vapor deposition at a substrate temperature of 400°C. The a-SiC:H has a mm-submm loss tangent ranging from $0.80\pm 0.01\times 10^{-4}$ to $1.43\pm 0.04\times 10^{-4}$ in the range of 270 to 385 GHz. The microwave loss tangent is $3.2\pm 0.2\times 10^{-5}$. These are the lowest low-power sub-kelvin loss tangents that have been reported for microstrip resonators at mm-submm and microwave frequencies. We observe that the loss tangent increases with frequency. The a-SiC:H films are free of blisters and have low stress: $-$20 MPa compressive at 200 nm thickness to 60 MPa tensile at 1000 nm thickness.

References in corpus (11)

• Supplementary information for "Quantum supremacy using a programmable superconducting processor"
• Microwave Dielectric Loss at Single Photon Energies and milliKelvin Temperatures
• Generalized Tunneling Model for TLS in amorphous materials and its predictions for their dephasing and the noise in superconducting microresonators
• Infrared dielectric properties of low-stress silicon nitride
• Superconducting NbTiN Thin Films with Highly Uniform Properties over a 100 mm diameter Wafer
• Phonon-trapping enhanced energy resolution in superconducting single photon detectors
• Thin film dielectric microstrip kinetic inductance detectors
• Wideband on-chip terahertz spectrometer based on a superconducting filterbank
• Full-Array Noise Performance of Deployment-Grade SuperSpec mm-wave On-Chip Spectrometers
• Suppression of radiation loss in high kinetic inductance superconducting co-planar waveguides
• Characterization of low-loss hydrogenated amorphous silicon films for superconducting resonators

Cited by in corpus (8)

• 2023 Astrophotonics Roadmap: pathways to realizing multi-functional integrated astrophotonic instruments
• Characterization of the low electric field and zero-temperature two-level-system loss in hydrogenated amorphous silicon
• Characterization of low-loss hydrogenated amorphous silicon films for superconducting resonators
• Geometry dependence of TLS noise and loss in a-SiC:H parallel plate capacitors for superconducting microwave resonators
• Vibrational modes as the origin of dielectric loss at 0.27$\unicode{x2013}$100 THz in a-SiC:H
• Measurement of Dielectric Loss in Silicon Nitride at Centimeter and Millimeter Wavelengths
• NEW-MUSIC: The Next-generation Extended-Wavelength Multiband Sub/millimeter Inductance Camera
• Fabrication Development for SPT-SLIM, a Superconducting Spectrometer for Line Intensity Mapping