Ferroelectricity in epitaxially strained rhombohedral ZrO2 thin films

Abstract

Zirconia and hafnia based thin films have attracted tremendous attention in the last decade due to their unexpected ferroelectric behavior at the nanoscale, which facilitates the downscaling of ferroelectric devices. The present work reports a novel ferroelectric rhombohedral phase of ZrO2 that can be achieved in thin films grown on (111)- Nb:SrTiO3 substrates by ion-beam sputtering. Structural and ferroelectric characterizations reveal that the (111)-oriented ZrO2 films are under epitaxial compressive strain and display a switchable ferroelectric polarization of about 20.2 μC/cm2 with a coercive field of 1.5 MV/cm. Moreover, the time dependent polarization reversal characteristics of Nb:STO/ZrO2/Au film capacitors exhibit bell-shape curves, a typical feature of ferroelectric films associated with domains reversal. The estimated activation field is comparable to the coercive field obtained from polarization-electric field hysteresis loops. Interestingly, the studied films show ferroelectric behavior per se, i.e., there is no need to apply the wake-up cycle that is essential to induce ferroelectricity in the conventional (orthorhombic) ferroelectric phase of ZrO2. Therefore, the present films have a technologically advantage over the previously studied ferroelectric ZrO2 films, and may be attractive for nanoscale ferroelectric devices.

arXiv comment26 pages, 9 figures

References in corpus (9)

• Restoring the density-gradient expansion for exchange in solids and surfaces
• Generalized gradient approximation for solids and their surfaces
• A rhombohedral ferroelectric phase in epitaxially-strained Hf0.5Zr0.5O2 thin films
• Effects of Strain and Film Thickness on the Stability of the Rhombohedral Phase of HfO2
• Direct epitaxial growth of polar (1-x)HfO2-(x)ZrO2 ultra-thin films on Silicon
• Guidelines for the stabilization of a polar rhombohedral phase in epitaxial Hf0.5Zr0.5O2 thin films
• Stabilization of phase-pure rhombohedral HfZrO4 in Pulsed Laser Deposited thin films
• Effect of Pt bottom electrode texture selection on the tetragonality and physical properties of Ba0.8Sr0.2TiO3 thin films produced by pulsed laser deposition
• Effect of dopant ordering on the stability of ferroelectric hafnia

Cited by in corpus (2)

• Stabilization of the epitaxial rhombohedral ferroelectric phase in ZrO2 by surface energy
• Electro-optic properties of ZrO2, HfO2 and LiNbO3 ferroelectric phases: A comprehensive and comparative study with density functional theory