Electrical manipulation of magnetic anisotropy in a Fe${}_{81}$Ga${}_{19}$/PMN-PZT magnetoelectric multiferroic composite

Abstract

Magnetoelectric composites are an important class of multiferroic materials that pave the way towards a new generation of multifunctional devices directly integrable in data storage technology and spintronics. This study focuses on strain-mediated electrical manipulation of magnetization in an extrinsic multiferroic. The composite includes 5 nm or 60 nm Fe${}_{81}$Ga${}_{19}$ thin films coupled to a piezoelectric (011)-PMN-PZT. The magnetization reversal study reveals a converse magnetoelectric coefficient ${\alpha }_{\mathrm{CME},\max }\approx 2.7\times 10^{-6}$ s.m${}^{-1}$ at room temperature. This reported value of ${\alpha }_{\mathrm{CME}}$ is among the highest so far compared to previous reports of single-phase multiferroics as well as composites. An angular dependency of ${\alpha }_{\mathrm{CME}}$ is also shown for the first time, arising from the intrinsic magnetic anisotropy of FeGa. The highly efficient magnetoelectric composite FeGa/PMN-PZT demonstrates drastic modifications of the in-plane magnetic anisotropy, with an almost 90${}^{\circ }$ rotation of the preferential anisotropy axis in the thinner films under an electric field E = 10.8 kV.cm${}^{-1}$. Also, the influence of thermal strain on the bilayer's magnetic coercivity is compared to that of a reference bilayer FeGa/Glass at cryogenic temperatures. A different evolution is observed as a function of temperature, revealing a substrate thermo-mechanical influence which has not yet been reported in FeGa thin films coupled to a piezoelectric material.

References in corpus (8)

• Giant sharp magnetoelectric switching in multiferroic epitaxial La_{0.67}Sr_{0.33}MnO_3 on BaTiO_3
• Influence of strain on magnetization and magnetoelectric effect in La0.7A0.3MnO3 / PMN-PT(001) (A = Sr; Ca)
• Electric field control of exchange bias in multiferroic epitaxial heterostructures
• Direct observation of nanometer-scale amorphous layers and oxide crystallites at grain boundaries in polycrystalline Sr1-xKxFe2As2 superconductors
• Experimental demonstration of complete 180 degree reversal of magnetization in isolated Co-nanomagnets on a PMN-PT substrate with voltage generated strain
• Non-volatile voltage control of magnetization and magnetic domain walls in magnetostrictive epitaxial thin films
• Electric field control of magnetic states in isolated and dipole-coupled FeGa nanomagnets delineated on a PMN-PT substrate
• Thickness dependence of magnetization reversal and magnetostriction in FeGa thin films

Cited by in corpus (1)

• Evidence for charge mediated coupling in Fe-Ga/PMN-PT composite multiferroic