Crystal structure instability of FeSe grains: Formation of non-superconducting phase at the grain surface

Abstract

We investigated the magnetization and crystal structure of FeSe polycrystalline samples with various grain sizes. For the samples with large grains, a large magnetic critical current density Jc was observed. For the samples with small grains, superconductivity signals were not observed; instead, magnetization hysteresis, which is not a result of superconductivity, was observed. In the X-ray diffraction pattern for the samples with small grains, broad additional peaks were observed, corresponding to the formation of the non-superconducting (monoclinic) Fe-Se phase at the FeSe grain surface. The crystal structure instability at the grain surface would be the reason for the low superconducting properties of the Fe-chalcogenide polycrystalline wires investigated thus far.

arXiv comment16 pages, 4 figures, 3 supplemental materials

References in corpus (26)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Interface induced high temperature superconductivity in single unit-cell FeSe films on SrTiO3
• Superconductivity in single-layer films of FeSe with a transition temperature above 100 K
• Superconductivity at 36 K in beta-Fe1.01Se with the compression of the interlayer separation under pressure
• Phase Diagram and High Temperature Superconductivity at 65 K in Tuning Carrier Concentration of Single-Layer FeSe Films
• Superconductivity at 27 K in tetragonal FeSe under high pressure
• To What Extent Iron-Pnictide New Superconductors Have Been Clarified: A Progress Report
• Extreme Sensitivity of Superconductivity to Stoichiometry in FeSe (Fe1+dSe)
• Tellurium substitution effect on superconductivity of the alpha-phase Iron Selenide
• Pressure evolution of low-temperature crystal structure and bonding of 37 K $T_c$ FeSe superconductor
• Anion height dependence of Tc for the Fe-based superconductor
• Exploration of new superconductors and functional materials and fabrication of superconducting tapes and wires of iron pnictides
• Superconductivity in S-substituted FeTe
• Superconductivity at T_c ~ 14 K in Single Crystalline FeTe${}_{0.61}$Se${}_{0.39}$
• Realization of practical level current densities in Sr0.6K0.4Fe2As2 tape conductors for high-field applications
• Fabrication of the iron-based superconducting wire using Fe(Se, Te)
• Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes
• Phase diagram and superconductivity at 58.1 K in α-FeAs free SmFeAsO1-xFx
• Effective Ex-Situ Fabrication of F-Doped SmFeAsO Wire for High Transport Critical Current Density
• Transport properties and microstructure of mono- and seven-core wires of FeSe1-xTex superconductor by Fe-diffusion powder-in-tube method
• High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process
• Low-temperature synthesis of SmFeAsO0.7F0.3 wires with high transport critical current density
• Fabrication of binary FeSe superconducting wires by novel diffusion process
• Transport properties of the single- and 3-core Fe-Se wires fabricated by a novel chemical-transformation PIT process
• Electrodeposition as a new route to synthesize superconducting FeSe
• Superconducting properties of FeSe wires and tapes prepared by gas diffusion technique