Co-co-doping effect for (Ca,RE)FeAs2 sintered bulk

Abstract

Superconducting properties of Co-co-doped (Ca,RE)FeAs2 ((Ca,RE)112: RE = La, Pr) were investigated. Co-co-doping increased Tc of (Ca,Pr)112 while Mn-co-doping suppressed superconductivity of (Ca,RE)112. Co-co-doped (Ca,La)112 showed large diamagnetic screening and sharper superconducting transition than Co-free (Ca,La)112. Tczero observed in resistivity measurements increased from 14 K to 30 K by Co-co-doping, while Tconset was not increased. The critical current density (Jc) of Co-co-doped (Ca,La)112 were approximately 2.1 x 104 Acm-2 and 3.2 x 103 Acm-2 at 2 K and 25 K, respectively, near zero field. These relatively high Jcs and large diamagnetic screening observed in susceptibility measurement as for polycrystalline bulks suggest bulk superconductivity of Co-co-doped (Ca,RE)112 compounds.

References in corpus (9)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity at 22 K in Co-doped BaFe2As2 Crystals
• Superconductivity in Co-doped LaFeAsO
• Structure and superconductivity of LiFeAs
• Superconductivity at 17 K in (Fe2P2)(Sr4Sc2O6): a new superconducting layered pnictide oxide with a thick perovskite oxide layer
• Superconductivity induced by cobalt doping in iron-based oxyarsenides
• Effect of Co doping on superconductivity and transport properties in SmFe${}_{1-x}$Co${}_x$AsO
• Superconducting Transition Temperatures of up to 47 K from Simultaneous Rare-Earth Element and Antimony Doping of 112-Type CaFeAs2
• Synthesis and physical properties of Ca1-xRExFeAs2 with RE = La ~ Gd