Enhancement of transport critical current density of SmFeAsO1-xFx tapes fabricated by an ex-situ powder-in-tube method with a Sn-presintering process

Abstract

SmFeAsO1-xFx (Sm1111) tapes were prepared by an ex-situ powder-in-tube method with a Sn-presintering process. Scanning electron microscopy revealed apparent difference in microstructure between Sn-presintered tapes and the previously reported polycrystalline Sm1111 bulk, since Sn has reduced FeAs wetting phase and filled the voids between Sm1111 grains. The Sn-presintered tapes showed significant enhanced field dependences of transport Jc compared with Sn-added tapes. A highest transport critical current density (Jc) of 3.45x10^4 A cm-2 at 4.2 K and self-field is achieved. Magneto-optical (MO) imaging further confirmed large and well-distributed global and intergranular Jc in Sn-presintered Sm1111 tapes.

19 pages, 7 figures

References in corpus (9)

• Nearly Isotropic superconductivity in (Ba,K)Fe2As2
• Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
• Upper critical fields and thermally-activated transport of Nd(O_0.7F_0.3)FeAs single crystal
• High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
• Critical Fields and Anisotropy of NdO0.82F0.18FeAs Single Crystals
• Single crystal of superconducting SmFeAsO1-xFy grown at high pressure
• Evidence for two distinct scales of current flow in polycrystalline Sm and Nd iron oxypnictides
• Biaxially textured cobalt-doped BaFe2As2 films with high critical current density over 1 MA/cm2 on MgO-buffered metal-tape flexible substrates
• Superconducting properties of SmO1-xFxFeAs wires with Tc = 52 K prepared by the powder-in-tube method