Refinement of Nb3Sn grain size by the generation of ZrO2 precipitates in Nb3Sn wires

Abstract

In this letter we demonstrate that if oxygen can be properly supplied to (Nb-Zr)-Sn wires, ZrO2 precipitates will form during the heat treatment, refining the Nb3Sn grain size markedly. Here, a Nb3Sn subelement was fabricated in which Nb-1Zr alloy was used, and oxygen was supplied via SnO2 powder. The results showed that such a design could supply sufficient oxygen to internally oxidize the Zr in the Nb-1Zr alloy, and that the sample reacted at 650 °C had grain sizes of ~45 nm, less than half the size of the grains in present Nb3Sn conductors. Magnetic measurements showed that the peak of the pinning force vs. field (Fp-B) curve was shifted to ~0.3Birr (the irreversibility field).

7 figures. Applied Physics Letter, Vol. 104, Issue 9, 2014

Cited by in corpus (11)

• Modern and Future Colliders
• A review and prospects for Nb3Sn superconductor development
• Internally Oxidized Nb3Sn Strands with Fine Grain Size and High Critical Current Density
• Beneficial influence of Hf and Zr additions to Nb4at.%Ta on the vortex pinning of Nb${}_3$Sn with and without an O source
• Concept for a Future Super Proton-Proton Collider
• Ternary Nb3Sn superconductors with artificial pinning centers and high upper critical fields
• Performance Boost in Industrial Multifilamentary Nb3Sn Wires due to Radiation Induced Pinning Centers
• $\text{Ab Initio}$ Theory of the Impact from Grain Boundaries and Substitutional Defects on Superconducting Nb${}_3$Sn
• APC Nb${}_3$Sn superconductors based on internal oxidation of Nb-Ta-Hf alloys
• Superconducting properties variation with A15 composition in Nb3Sn
• Achievement of FCC specification in critical current density for Nb3Sn superconductors with artificial pinning centers