APC NbSn superconductors based on internal oxidation of Nb-Ta-Hf alloys
arXiv:2301.02571 · doi:10.1088/1361-6668/acb17a
Abstract
In the last few years, a new type of NbSn superconducting composite, containing a high density of artificial pinning centers (APC) generated via an internal oxidation approach, has demonstrated a significantly superior performance relative to present, state-of-the-art commercial NbSn conductors. This was achieved via the internal oxidation of Nb-4at.%Ta-1at.%Zr alloy. On the other hand, our recent studies have shown that internal oxidation of Nb-Ta-Hf alloys can also lead to dramatic improvements in NbSn performance. In this work we follow up this latter approach, fabricating a 61-stack APC wire based on the internal oxidation of Nb-4at.%Ta-1at.%Hf alloy, and compare its critical current density (Jc) and irreversibility field (Birr) with APC wires made using Nb-4at.%Ta-1at.%Zr. A second goal of this work was to improve the filamentary design of APC wires in order to improve their wire quality and electromagnetic stability. Our new modifications have led to significantly improved RRR and stability in the conductors, while still keeping non-Cu Jc at or above the FCC Jc specification. Further improvement via optimization of the wire recipe and design is ongoing. Finally, additional work needed to make APC conductors ready for applications in magnets is discussed.
arXiv commentMatches published version
References in corpus (5)
- A review and prospects for Nb3Sn superconductor development
- Refinement of Nb3Sn grain size by the generation of ZrO2 precipitates in Nb3Sn wires
- Internally Oxidized Nb3Sn Strands with Fine Grain Size and High Critical Current Density
- Beneficial influence of Hf and Zr additions to Nb4at.%Ta on the vortex pinning of NbSn with and without an O source
- Ternary Nb3Sn superconductors with artificial pinning centers and high upper critical fields