Graded Orbital Occupation near Interfaces in a La2NiO4 - La2CuO4 Superlattice

Abstract

X-ray absorption spectroscopy and resonant soft x-ray reflectivity show a non-uniform distribution of oxygen holes in a La2NiO4 - La2CuO4 (LNO-LCO) superlattice, with excess holes concentrated in the LNO layers. Weak ferromagnetism with Tc = 160 K suggests a coordinated tilting of NiO6 octahedra, similar to that of bulk LNO. Ni d3z2-r2 orbitals within the LNO layers have a spatially variable occupation. This variation of the Ni valence near LNO-LCO interfaces is observed with resonant soft x-ray reflectivity at the Ni L edge, at a reflection suppressed by the symmetry of the structure, and is possible through graded doping with holes, due to oxygen interstitials taken up preferentially by inner LNO layers. Since the density of oxygen atoms in the structure can be smoothly varied with standard procedures, this orbital occupation, robust up to at least 280 K, is tunable.

11 pages, 8 figures

References in corpus (8)

• High Mobility in LaAlO3/SrTiO3 Heterostructures: Origin, Dimensionality and Perspectives
• Orbital order and possible superconductivity in LaNiO3/LaMO3 superlattices
• Dimensionality Control of Electronic Phase Transitions in Nickel-Oxide Superlattices
• Orbital reflectometry
• Electronic reconstruction at SrMnO3-LaMnO3 superlattice interfaces
• Superconducting transition at 38 K in insulating-overdoped La2CuO4-La1.64Sr0.36CuO4 superlattices: Evidence for interface electronic redistribution from resonant soft x-ray scattering
• Lattice polarization effects on electron-gas charge densities in ionic superlattices
• Charge and spin stripe in La${}_{2-x}$Sr${}_x$NiO${}_4$ (x=1/3,1/2)

Cited by in corpus (2)

• Interface Ferromagnetism in a SrMnO3/LaMnO3 Superlattice
• Distinct oxygen hole doping in different layers of $\mathrm{S}{\mathrm{r}}_2\mathrm{Cu}{\mathrm{O}}_{4-\delta }-\mathrm{L}{\mathrm{a}}_2\mathrm{Cu}{\mathrm{O}}_4$ superlattices