Thickness-dependent Local Surface Electronic Structures of Homoepitaxial SrTiO3 Thin Films
arXiv:1004.2746 · doi:10.1063/1.3485826
Abstract
We have investigated the atomically-resolved substrate and homoepitaxial thin film surfaces of SrTiO3(001) using low-temperature scanning tunneling microscopy/spectroscopy (STM/STS) combined with pulsed laser deposition (PLD). It was found that annealing at 1000 oC in an oxygen partial pressure of 1*10-6 Torr, which is a typical annealing treatment for the preparation of SrTiO3 substrates, unexpectedly resulted in a disordered surface on an atomic scale. In contrast, homoepitaxial SrTiO3 thin films grown on this disordered substrate exhibited (2*2) surface reconstructions. The differential conductance spectra, dI/dV in STS measurements, revealed a number of surface defects in a 10-unit-cell-thick SrTiO3 film, but much fewer in a 50-unit-cell-thick film. These results indicate that the defect density in the film strongly depends on the film thickness, suggesting non-uniform stoichiometry along the growth direction.
17 pages, 4 figures
References in corpus (5)
- Magnetic effects at the interface between nonmagnetic oxides
- Electric Field Control of the LaAlO/SrTiO Interface Ground State
- High Mobility in LaAlO3/SrTiO3 Heterostructures: Origin, Dimensionality and Perspectives
- Electronic properties of buried hetero-interfaces of LaAlO3 on SrTiO3
- Atomically Resolved Surface Structure of SrTiO3(001) Thin Films Grown in Step-Flow Mode by Pulsed Laser Deposition