The influence of Ga${}^{+}$-irradiation on the transport properties of mesoscopic conducting thin films

Abstract

We studied the influence of 30keV Ga${}^{+}$-ions -- commonly used in focused ion beam (FIB) devices -- on the transport properties of thin crystalline graphite flake, La${}_{0.7}$Ca${}_{0.3}$MnO${}_3$ and Co thin films. The changes of the electrical resistance were measured in-situ during irradiation and also the temperature and magnetic field dependence before and after irradiation. Our results show that the transport properties of these materials strongly change at Ga${}^{+}$ fluences much below those used for patterning and ion beam induced deposition (IBID), limiting seriously the use of FIB when the intrinsic properties of the materials of interest are of importance. We present a method that can be used to protect the sample as well as to produce selectively irradiation-induced changes.

arXiv comment14 pages, 11 figures, will be published in Nanotechnology 2010

References in corpus (1)

• Sample Size Effects on the Transport Characteristics of Mesoscopic Graphite Samples

Cited by in corpus (7)

• Evidence of Josephson-coupled superconducting regions at the interfaces of Highly Oriented Pyrolytic Graphite
• Evidence for semiconducting behavior with a narrow band gap of Bernal graphite
• Granular superconductivity at room temperature in bulk highly oriented pyrolytic graphite samples
• Ballistic transport at room temperature in micrometer size multigraphene
• Length dependence of the resistance in graphite: Influence of ballistic transport
• Invited review: Graphite and its hidden superconductivity
• Electrical properties of in-plane-implanted graphite nanoribbons