Theoretical study of kinks on screw dislocation in silicon

Abstract

Theoretical calculations of the structure, formation and migration of kinks on a non-dissociated screw dislocation in silicon have been carried out using density functional theory calculations as well as calculations based on interatomic potential functions. The results show that the structure of a single kink is characterized by a narrow core and highly stretched bonds between some of the atoms. The formation energy of a single kink ranges from 0.9 to 1.36 eV, and is of the same order as that for kinks on partial dislocations. However, the kinks migrate almost freely along the line of an undissociated dislocation unlike what is found for partial dislocations. The effect of stress has also been investigated in order to compare with previous silicon deformation experiments which have been carried out at low temperature and high stress. The energy barrier associated with the formation of a stable kink pair becomes as low as 0.65 eV for an applied stress on the order of 1 GPa, indicating that displacements of screw dislocations likely occur via thermally activated formation of kink pairs at room temperature.

References in corpus (8)

• Interatomic Potential for Silicon Defects and Disordered Phases
• Environment Dependent Interatomic Potential for Bulk Silicon
• First principles determination of the Peierls stress of the shuffle screw dislocation in silicon
• Core reconstruction of the 90-degree partial dislocation in non-polar semiconductors
• Undissociated screw dislocations in silicon: calculations of core structure and energy
• Temperature effects on dislocation core energies in silicon and germanium
• Stability of undissociated screw dislocations in zinc-blende covalent materials from first principle simulations
• Models of core reconstruction for the 90-degree partial dislocation in semiconductors

Cited by in corpus (4)

• Unveiling the mechanisms of motion of synchro-Shockley dislocations in Laves phases
• Room-temperature dislocation plasticity in ceramics: Methods, Materials, and Mechanisms
• Bowl breakout, escaping the positive region when searching for saddle points
• Diffusion Mechanisms in Li${}_{0.5}$CoO${}_2$ -- A Computational Study