Effect of stoichiometry on oxygen incorporation in MgB2 thin films

Abstract

The amount of oxygen incorporated into MgB2 thin films upon exposure to atmospheric gasses is found to depend strongly on the material's stoichiometry. Rutherford backscattering spectroscopy was used to monitor changes in oxygen incorporation resulting from exposure to: (a) ambient atmosphere, (b) humid atmospheres, (c) anneals in air and (d) anneals in oxygen. The study investigated thin-film samples with compositions that were systematically varied from Mg0.9B2 to Mg1.1B2. A significant surface oxygen contamination was observed in all of these films. The oxygen content in the bulk of the film, on the other hand, increased significantly only in Mg rich films and in films exposed to humid atmospheres.

arXiv comment10 pages, 6 figures, 1 table

References in corpus (11)

• Superconductivity in Dense $Mg{B}_2$ Wires
• In situ epitaxial MgB2 thin films for superconducting electronics
• High-field superconductivity in alloyed MgB2 thin films
• Microstructure and Structural Defects in MgB2 Superconductor
• Direct observation of nm-scale Mg- and B-oxide phases at grain boundaries in MgB2
• Growth of high quality large area MgB2 thin films by reactive evaporation
• Observation of coherent oxide precipitates in polycrystalline MgB2
• Thermochemistry of MgB2 Thin Film Synthesis
• Effect of damage by 2-MeV He ions on the normal and superconducting properties of magnesium diboride
• Effect of damage by 2-MeV He ions and annealing on Hc2 in MgB2 thin films
• Nonstoichiometry, Defects and Transport Properties in MgB2