S. Hosono

activity

20142016

most citedSynthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K

84 citations · 216 across the 5 of their papers we have counts for

collaborators

5 papers

cond-mat.supr-con2016★ 12 cited

Superconductivity and Intercalation Statein the Lithium-Hexamethylenediamine-Intercalated Superconductor Li $_{x}$ (C $_{6}$ H $_{16}$ N $_{2}$ ) $_{y}$ Fe $_{2 - z}$ Se $_{2}$ : Dependence on the Intercalation Temperature and Lithium Content

Shohei Hosono, Takashi Noji, Takehiro Hatakeda +3

The superconductivity and intercalation statein the lithium-and hexamethylenediamine (HMDA)-intercalated superconductor Li $_{x}$ (C $_{6}$ H $_{16}$ N $_{2}$ ) $_{y}$ Fe $_{2 - z}$ Se $_{2}$ have been inv…

cond-mat.supr-con2016★ 42 cited

New Superconducting Phase of Li $_{x}$ (C $_{6}$ H $_{16}$ N $_{2}$ ) $_{y}$ Fe $_{2 - z}$ Se $_{2}$ with $T_{c}$ = 41 K Obtained through the Post-Annealing

Shohei Hosono, Takashi Noji, Takehiro Hatakeda +3

Post-annealing effects on the crystal structure and superconductivity of the lithium- and hexamethylenediamine (HMDA)-intercalated superconductor Lix(C6H16N2)yFe2-zSe2 have been in…

cond-mat.supr-con2015★ 13 cited

Resistive superconducting transition and effects of atmospheric exposure in the intercalation superconductor Ax(C2H8N2)yFe2-zSe2 (A = Li, Na)

T. Hatakeda, T. Noji, S. Hosono +3

We have succeeded in observing zero-resistivity in newly discovered intercalation superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K, using the sintered pellet samples…

cond-mat.supr-con2015★ 65 cited

New intercalation superconductor Lix(C6H16N2)yFe2-zSe2 with a very large interlayer-spacing and Tc = 38 K

S. Hosono, T. Noji, T. Hatakeda +3

A new iron-based superconductor, Lix(C6H16N2)yFe2-zSe2, with Tc = 38 K has successfully been synthesized via the intercalation of lithium and hexamethylenediamine into FeSe. The su…

cond-mat.supr-con2014★ 84 cited

Synthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K

Takashi Noji, Takehiro Hatakeda, Shohei Hosono +3

New iron-based intercalation superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K have successfully been synthesized via intercalation of dissolved alkaline metal in eth…

Superconductivity and Intercalation Statein the Lithium-Hexamethylenediamine-Intercalated Superconductor Lix​(C6​H16​N2​)y​Fe2−z​Se2​: Dependence on the Intercalation Temperature and Lithium Content

New Superconducting Phase of Lix​(C6​H16​N2​)y​Fe2−z​Se2​ with Tc​ = 41 K Obtained through the Post-Annealing

Resistive superconducting transition and effects of atmospheric exposure in the intercalation superconductor Ax(C2H8N2)yFe2-zSe2 (A = Li, Na)

New intercalation superconductor Lix(C6H16N2)yFe2-zSe2 with a very large interlayer-spacing and Tc = 38 K

Synthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K

Superconductivity and Intercalation Statein the Lithium-Hexamethylenediamine-Intercalated Superconductor Li $_{x}$ (C $_{6}$ H $_{16}$ N $_{2}$ ) $_{y}$ Fe $_{2 - z}$ Se $_{2}$ : Dependence on the Intercalation Temperature and Lithium Content

New Superconducting Phase of Li $_{x}$ (C $_{6}$ H $_{16}$ N $_{2}$ ) $_{y}$ Fe $_{2 - z}$ Se $_{2}$ with $T_{c}$ = 41 K Obtained through the Post-Annealing