Development and geometry of isotropic and directional shrinkage crack patterns

Abstract

We have studied shrinkage crack patterns which form when a thin layer of an alumina/water slurry dries. Both isotropic and directional drying were studied. The dynamics of the pattern formation process and the geometric properties of the isotropic crack patterns are similar to what is expected from recent models, assuming weak disorder. There is some evidence for a gradual increase in disorder as the drying layer become thinner, but no sudden transition, in contrast to what has been seen in previous experiments. The morphology of the crack patterns is influenced by drying gradients and front propagation effects, with sharp gradients having a strong orienting and ordering effect.

8 pages, 11 figures, 8 in jpg format, 3 in postscript. See also http://mobydick.physics.utoronto.ca/mud.html

References in corpus (1)

• Fracture Patterns Induced by Desiccation in a Thin Layer

Cited by in corpus (29)

• Evolving fracture patterns: columnar joints, mud cracks, and polygonal terrain
• Spiral cracks in drying precipitates
• An Experimental Investigation of the Scaling of Columnar Joints
• Self-replicating cracks: a collaborative fracture mode in thin films
• Order and disorder in columnar joints
• Frozen impacted drop: From fragmentation to hierarchical crack patterns
• Stable propagation of an ordered array of cracks during directional drying
• Universal Scaling of Polygonal Desiccation Crack Patterns
• Crack patterns over uneven substrates
• Modeling the buckling and delamination of thin films
• On maturation of crack patterns
• Characterisation of spatial network-like patterns from junctions' geometry
• Effect of Interaction on the Formation of Memories in Paste
• Origin of crack pattern in the deposition from drying colloidal suspension
• Salt polygons and porous media convection
• Eliminating cracking during drying
• A model for hierarchical patterns under mechanical stresses
• A new failure mechanism in thin film by collaborative fracture and delamination: interacting duos of cracks
• Attractive and repulsive cracks in a heterogeneous material
• Morphometric analysis of polygonal cracking patterns in desiccated starch slurries
• Asymptotic analysis of stresses near a crack tip in a two dimensional colloidal packing saturated with liquid
• Morphologies of expansion ridges of elastic thin films onto a substrate
• Flow velocity-dependent transition of anisotropic crack patterns in CaCO${}_3$ pastes
• The geometry of soil crack networks
• Universal fluctuation of polygonal crack geometry in solidified lava
• Desiccation of a clay film: Cracking versus peeling
• Wettability Induced Crack Dynamics and Morphology
• Memory of rotation in residual stress of paste
• Fragment size density estimator for shrinkage-induced fracture based on a physics-informed neural network